Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 50% RH, | ASTM D 570 | 0.4 | % |
| Moisture Absorption | 23°C / 50 | ISO 62 | 0.74 | % |
| Modeling Shrinkage(Across Flow) | flow, 24 h | ASTM D 955 | 0.3 | % |
| Modeling Shrinkage(Across Flow) | flow, 24 h | ISO 294 | 0.34 | % |
| Modeling Shrinkage (Across Flow) | xflow, 24 | ASTM D 955 | 1.2 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength(Break) | / | ASTM D638 | 197 | Mpa |
| Tensile Strength(Break) | / | ISO 527 | 194 | Mpa |
| Tensile Elongation (Break) | / | ASTM D638 | 2.4 | % |
| Tensile Elongation (Break) | / | ISO 527 | 2.4 | % |
| Tensile Modulus | 50 mm/m | ASTM D638 | 17650 | Mpa |
| Tensile Modulus | 1 mm/min | ISO 527 | 14000 | Mpa |
| Flexural Modulus | / | ASTM D790 | 12540 | Mpa |
| Flexural Modulus | / | ISO 178 | 14500 | Mpa |
| Flexural Strength | / | ASTM D790 | 312 | Mpa |
| Flexural Strength | / | ISO 178 | 300 | Mpa |
| Flammability Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | | UL94 | 1.5 | mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod Impact Strength | 23℃ (73℉) | ASTM D256 | 149 | |
| Notched Izod Impact Strength | 23℃ (73℉)80*10*4 | ISO 180/1A | 13 | |
| Unnotched Izod Impact Strength | 23℃ (73℉)80*10*4 | ISO 180/1U | 65 | kJ/m² |
| Unnotched Izod Impact Strength | 23℃ (73℉) | ASTM D4812 | 1585 | |
| Instrumented Dart Impact (23℃) | / | ASTM D3763 | 12 | J |
| Multi-Axial Instrumented Impact Energy | / | ISO 6603 | 3 | J |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Coefficient of Linear Thermal Expansion(Flow) | -40°C to | ASTM E831 | 27 E-6 | °C |
| Coefficient of Linear Thermal Expansion(Flow) | -40°C to | ISO 11359-2 | 28.1 E-6 | °C |
| Coefficient of Linear Thermal Expansion(Across Flow) | -40°C to | ASTM E831 | 43.2 E-6 | °C |
| Coefficient of Linear Thermal Expansion(Across Flow) | -40°C to | ISO 11359-2 | 44.2 E-6 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.