Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD2：23°C,72小时 | ISO2577 | 0.60到1.1 | % |
| Density | | ISO1183 | 1.35 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | 屈服 | ISO527-2/5 | 245 | Mpa |
| Tensile Stress | 断裂 | ISO527-2/5 | 180 | Mpa |
| Tensile Strain | 断裂 | ISO527-2/5 | 3.0 | % |
| Tensile Modulus | | ISO527-2/1 | 10000 | Mpa |
| Flexural Modulus | | ISO178 | 8500 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45MPa,未退火 | ISO75-2/B | 255 | °C |
| Deflection Temperature Under Load? | 1.8MPa,未退火 | ISO75-2/A | 250 | °C |
| Melting temperature | | ISO11357-3 | 258到262 | °C |
| Vicat Softening Temperature | | ISO306/B50 | 255 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Comparative Tracking Index | 解决方案A | IEC60112 | 500 | V |
| Surface Resistivity | | IEC60093 | 1E+13 | ohms |
| Volume Resistivity | | IEC60093 | 1E+15 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod impact strength | 23°C | ISO180/1U | 50 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 11 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Glow Wire Flammability Index | 1.0到3.0mm | IEC60695-2-12 | 650 | °C |
| Burning Rate | | FMVSS302 | <100 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.