PA66 TORZEN® G3300 L INVISTA USA
85
- Unit Price:
- $3320 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Filler: Glass fiber reinf 33% filler by weight
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | 正常: 2.00 mm | ISO 294-4 | 0.90 到 1.10 | % |
| 平行: 2.00 mm | ISO 294-4 | 0.30到 0.40 | % | |
| TD:2.00mm | ISO294-4 | 0.90到1.1 | % | |
| MD:2.00mm | ISO294-4 | 0.30到0.40 | % | |
| Moisture Absorption | 23°C,24hr | ISO62 | 1.2 | % |
| 23℃, 24 hr | ISO 62 | 1.2 | % | |
| Equilibrium, 23℃, 50% RH | ISO 62 | 1.8 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 1.8 | % | |
| glass fiber content | ISO3451/4 | 33 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -40℃ | ISO 179 | 10 | kJ/m² |
| 23℃ | ISO 179 | 12 | kJ/m² | |
| Notched Izod Impact Strength | 23℃ | ISO 180 | 12 | kJ/m² |
| Flexural Stress | ISO178 | 285 | Mpa | |
| Tensile Strength(Break) | ISO 527 | 205 | Mpa | |
| Elongation at break | ISO 527 | 3.1 | % | |
| Tensile Stress | Break | ISO527-2 | 205 | Mpa |
| Tensile Strain | Break | ISO527-2 | 3.1 | % |
| Tensile Modulus | ISO 527 | 10500 | Mpa | |
| ISO527-2 | 10500 | Mpa | ||
| Flexural Modulus | ISO178 | 9500 | Mpa | |
| ISO 178 | 9500 | Mpa | ||
| Flexural Strength | ISO 178 | 285 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed | ISO 75 | 255 | °C |
| 1.82 MPa, Unannealed | ISO 75 | 248 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 248 | °C | |
| 0.45MPa,Unannealed | ISO75-2/B | 255 | °C | |
| Melting temperature | ISO11357-3 | 262 | °C | |
| Melting Temperature | 10℃/min | ISO 11357 | 262 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.