| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | 23℃ | % | 0.10到0.31 | |
| Saturation ,23℃ | | % | 3.5到5.0 | |
| Flow,23℃,50%RH | | % | 1.2到1.5 | |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | Break,23℃ | MPa | 144.83到292.41 | |
| Tensile Strain | Break,23℃ | % | 1.9到3.1 | |
| Tensile Modulus | 23℃ | MPa | 8206.9到28000.0 | |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melting temperature | | °C | 260 | |
| Continuous Use Temperature | | °C | 110到220 | |
| 8.0Mpa, Unannealed | | °C | 65到220 | |
| Flow | | mm/mm/°C | 68.6E-5到127.0E-5 | |
| Flow | | mm/mm/°C | 142.2E-5到203.2E-5 | |
| 1.8MPa, Unannealed | | °C | 230到250 | |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Strength | 23℃ | V/mil | 840 | |
| Volume Resistivity | 23℃ | ohms·cm | 1.0E+12到1.0E+14 | |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | 23℃ | kJ/m² | 11.143到19.964 | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball Indentation Hardness | | MPa | 222.76到370.34 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.