PA66 INVISTA™ G5000HSL NC01 INVISTA ARGENTINA
30
- Unit Price:
- $3955 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | 垂直Flow : 2.00 mm | ISO 294-4 | 0.80 到 0.90 | % |
| Flow : 2.00 mm | ISO 294-4 | 0.20 到 0.30 | % | |
| Water absorption rate | 23°C, 24 hr | ISO 62 | 0.65 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 1.1 | % | |
| Melt flow rate | 280°C/5.0 kg | ASTM D1238 | 2.3 | g/10 min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO 527-2 | 16900 | Mpa | |
| Bending modulus | ISO 178 | 16700 | Mpa | |
| Bending stress | ISO 178 | 350 | Mpa | |
| Tensile stress (fracture) | ISO 527-2 | 247 | Mpa | |
| Tensile strain (fracture) | ISO 527-2 | 2.4 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting temperature | ISO 11357-3 | 262 | °C | |
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 260 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 255 | °C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying time | 3.0 到 4.0 | hr | ||
| Temperature at the rear of the barrel | 250 到 270 | °C | ||
| Temperature in the middle of the barrel | 270 到 290 | °C | ||
| Temperature at the front of the material cylinder | 270 到 290 | °C | ||
| Spray nozzle temperature | 270 到 290 | °C | ||
| Back pressure | 0.200 到 1.00 | Mpa | ||
| Exhaust hole depth | 7.0E-3 到 0.040 | mm | ||
| cushion | 4.00 到 6.00 | mm | ||
| drying temperature | 80 | °C | ||
| Suggested maximum moisture content | 0.080 到 0.18 | % | ||
| Processing (melt) temperature | 280 到 300 | °C | ||
| Mold temperature | 50.0 到 90.0 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | 100 | kJ/m² |
| 23°C | ISO 179 | 130 | kJ/m² | |
| Impact strength of cantilever beam gap (23 ° C) | ISO 180 | 13 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.