Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | Across Flow | 内部方法 | 0.70 | % |
Modeling Shrinkage | 流量 | 内部方法 | 0.40 | % |
Moisture Absorption | Saturation, 23°C | | -- | % |
Moisture Absorption | Equilibrium, 23°C, 50% RH | ISO 62 | -- | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Break, 23°C | ISO 527-2 | 237 | Mpa |
Tensile Stress | -- | ASTM D638 | 235 | Mpa |
Tensile Modulus | 23°C | ISO 527-2 | 16900 | Mpa |
Tensile Elongation | Break | ASTM D638 | 2.5 | % |
Tensile Elongation | Break, 23°C | ISO 527-2 | 2.0 | % |
Flexural Modulus | -- | ASTM D790 | 14500 | Mpa |
Flexural Modulus | 23°C | ISO 178 | 13600 | Mpa |
Flexural Strength | -- | ASTM D790 | 390 | Mpa |
Flexural Strength | 23°C | ISO 178 | 371 | Mpa |
Taber Abrasion Resistance | 1000 Cycles | ASTM D1044 | -- | mg |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45 MPa, Unannealed | ASTM D648, ISO 75-2/B | 260 | °C |
Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ASTM D648 | 250 | °C |
Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ISO 75-2/A | 255 | °C |
Coefficient of Linear Thermal Expansion (Flow) | | ASTM D696 | 2.0E-5 | cm/cm/°C |
Thermal Conductivity | | | 0.40 | W/m/K |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | ASTM D257, IEC 60093 | 1.0E+15 | ohms |
Volume Resistivity | -- | ASTM D257 | 1.0E+15 | ohms·cm |
Volume Resistivity | 23°C | IEC 60093 | 1.0E+15 | ohms·cm |
Comparative Tracking Index | 3.00 mm | IEC 60112 | 525 | V |
Dielectric Strength | | ASTM D149, IEC 60243-1 | 21 | KV/mm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | | ISO 179 | 无断裂 | |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | M-Scale | ASTM D785 | 95 | |
Rockwell Hardness | R-Scale | ASTM D785 | 118 | |
Rockwell Hardness | M -Sale | ISO 2039-2 | 95 | |
Rockwell Hardness | R -Sale | ISO 2039-2 | 118 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 0.75 mm | UL 94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.