PA66 Zytel® WRF403 NC010 DUPONT USA
94
- Unit Price:
- $9925 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced High rigidity
- Application Areas:Automotive Applications sporting goods
- Color:--
- Grade:Wear resistant grade
Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.50 | ||
| Molding shrinkage rate | ASTM D955 | 0.3~0.8 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | (Dry)，（Flow） | ISO 294-4 | 0.30 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Gap impact strength | (Dry) | ISO 180 | 13.0 | kJ/m² |
| Charpy notch impact strength | (Dry) | ISO 179 | 11.0 | kJ/m² |
| Non notched impact strength | (Dry) | ISO 180 | 70.0 | kJ/m² |
| Fracture point tensile strain | (Dry) | ISO 527-1, -2 | 2.8 | % |
| Fracture point tensile stress | (Dry) | ISO 527-1, -2 | 185 | Mpa |
| elongation at break | ASTM D638/ISO 527 | 2.8 | % | |
| Tensile modulus | ASTM D638/ISO 527 | 10300 | kg/cm²(MPa)[Lb/in²] | |
| (Dry) | ISO 527-1, -2 | 10300 | Mpa | |
| tensile strength | ASTM D638/ISO 527 | 185 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 9200 | kg·cm/cm(J/M)ft·lb/in | |
| (Dry) | ISO 178 | 9200 | Mpa | |
| bending strength | (Dry) | ISO 178 | 270 | Mpa |
| ASTM D790/ISO 178 | 270 | kg·cm/cm(J/M)ft·lb/in | ||
| Charpy impact strength | ASTM D256/ISO 179 | 13 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 80 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature/A | 1.80 Mpa，Unannealed(Dry) | ISO 75A-1, -2 | 250 | °C |
| Hot deformation temperature | ASTM D648/ISO 75 | 250 | ℃（℉） | |
| melting point | 263 | ℃（℉） | ||
| Melting temperature | (Dry) | ISO 3146 | 263 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.