Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD | 内部方法 | 0.90 | % |
| Modeling Shrinkage | MD | 内部方法 | 0.30 | % |
| Modeling Shrinkage | 吸水率(Saturation,23°C) | 内部方法 | -- | % |
| Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | -- | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | Break,23°C | ISO527-2 | 203 | Mpa |
| Tensile Strain | Break,23°C | ISO527-2 | 4.0 | % |
| Tensile Modulus | 23°C | ISO527-2 | 9500 | Mpa |
| Tensile Elongation | Break | ASTMD638 | 3.0 | % |
| Flexural Modulus | | ASTMD790 | 8400 | Mpa |
| Flexural Modulus | 23°C | ISO178 | 9700 | Mpa |
| Flexural Strength | | ASTMD790 | 309 | Mpa |
| Flexural Stress | 23°C | ISO178 | 296 | Mpa |
| Tensile Strength | | ASTMD638 | 215 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear thermal expansion coefficient | MD | ASTMD696 | 2E-05 | cm/cm/°C |
| Thermal Conductivity | | | 0.40 | W/m/K |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ASTMD648 | 208 | °C |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 208 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | | ISO179 | 92 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R-Scale | ASTMD785 | 121 | |
| Rockwell Hardness | M-Sale | ISO2039-2 | 97 | |
| Rockwell Hardness | R-Sale | ISO2039-2 | 121 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.