PA66 Durethan® D.AKV30H1.0 LANXESS WUXI

Unit Price:
$4246 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
38.2MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Filler: Glass fiber reinf 30% Filler by weight
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD:280°C,3.00mm2	ISO2577	1.5	%
	Modeling Shrinkage	TD:120°C,2hr,3.00mm3	ISO294-4	0.050	%
		Modeling Shrinkage	MD:280°C,3.00mm2	ISO2577	0.35	%
		Modeling Shrinkage	Modeling Shrinkage	MD:120°C,2hr,3.00mm3	ISO2577	0.040	%
Moisture Absorption	Saturation,23°C	ISO62	5.5	%
Moisture Absorption	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	2.0	%
Apparent Density		ISO60	0.70	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Stress	Break,23°C	ISO527-2/5	185	Mpa
Tensile Strain	Break,23°C	ISO527-2/5	3.0	%
Tensile Modulus	23°C	ASTMD638	10300	Mpa
Tensile Modulus	Tensile Modulus	23°C	ISO527-2/1	10600	Mpa
Tensile Elongation	Break,23°C	ASTMD638	3.0	%
Flexural Modulus	23°C	ASTMD790	841	Mpa
Flexural Strength	23°C	ASTMD790	290	Mpa
Tensile Strength	Break,23°C	ASTMD638	179	Mpa
Flexural Stress	3.5%Strain	ISO178/A	--	Mpa
	Flexural Stress	23°C	ISO178	290	Mpa
	Flexural Stress	Flexural Stress	FlexuralStrainatFlexuralStrength5(23°C)		4.0	%
Flexural Modulus	23°C	ISO178/A	8400	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature		ISO306/B120	>230	°C
Linear thermal expansion coefficient	MD：23to55°C	ISO11359-2	2.5E-05	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD：23to55°C	ISO11359-2	1E-04	cm/cm/°C
Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	250	°C
	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	250	°C
	Deflection Temperature Under Load?	Deflection Temperature Under Load?	8.0MPa,Unannealed	ISO75-2/C	135	°C
Melting Temperature		ISO11357-3	263	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface Resistivity		IEC60093	1E+14	ohms
Volume Resistivity	23°C	IEC60093	1E+15	ohms·cm
Dielectric Strength	23°C,1.00mm	IEC60243-1	40	KV/mm
Relative Permittivity	23°C,100Hz	IEC60250	4.00
Relative Permittivity	Relative Permittivity	23°C,1MHz	IEC60250	4.00
Comparative Tracking Index	SolutionA	IEC60112	600	V
Dissipation Factor?	23°C,1MHz	IEC60250	0.018
Dissipation Factor?	Dissipation Factor?	23°C,100Hz	IEC60250	9E-03

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	70	kJ/m²
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	90	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Ball Indentation Hardness		ISO2039-1	230	Mpa

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.6mm	UL94	HB
UL flame retardant rating	UL flame retardant rating	3.2mm	UL94	HB
Glow Wire Flammability Index	2.0mm	IEC60695-2-12	600	°C
Oxygen Index		ISO4589-2	23	%

Supplementary information	Test Condition	Test Method	Test Result	Unit
ISO Shortname		ISO1874	PA66,GR,14-110,GF30

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.