PA66 D.AKV30H2.0 BK LANXESS USA
37
- Unit Price:
- $3538 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 16.1MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Modeling Shrinkage | TD:290°C,2.00mm2 | ISO294-4 | 0.93 | % |
TD:120°C,2hr,2.00mm3 | ISO294-4 | 0.13 | % | |
MD:290°C,2.00mm2 | ISO294-4 | 0.39 | % | |
MD:120°C,2hr,2.00mm3 | ISO294-4 | 0.070 | % | |
Moisture Absorption | Saturation,23°C | ISO62 | 5.5 | % |
Equilibrium,23°C,50%RH | ISO62 | 2.0 | % | |
Apparent Density | ISO60 | 0.70 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Nominal Tensile Strain at Break | 23°C | ISO527-2/50 | 4.4 | % |
Flexural Modulus | 23°C | ISO178/A | 9200 | Mpa |
Tensile Modulus | 23°C | ASTMD638 | 9170 | Mpa |
Flexural Stress | 3.5%Strain | ISO178/A | 265 | Mpa |
23°C | ISO178 | 270 | Mpa | |
FlexuralStrainatFlexuralStrength6(23°C) | 4.0 | % | ||
Tensile Stress | Break,23°C | ISO527-2/5 | 175 | Mpa |
Tensile Strain | Break,23°C | ISO527-2/5 | 3.0 | % |
Tensile Modulus | 23°C | ISO527-2/1 | 10000 | Mpa |
Tensile Elongation | Break,23°C | ASTMD638 | 3.0 | % |
Flexural Modulus | 23°C | ASTMD790 | 8690 | Mpa |
Flexural Strength | 23°C | ASTMD790 | 270 | Mpa |
Tensile Strength | Break,23°C | ASTMD638 | 170 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Vicat Softening Temperature | -- | ISO306/B50 | 230 | °C |
-- | ISO306/B120 | >230 | °C | |
Linear thermal expansion coefficient | MD:23to55°C | ISO11359-2 | 3E-05 | cm/cm/°C |
TD:23to55°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
RTIElec | 0.75mm | UL746 | 125 | °C |
1.5mm | UL746 | 125 | °C | |
Evolution Calendar intelligent importer | 0.75mm | UL746 | 90.0 | °C |
1.5mm | UL746 | 105 | °C | |
RTIStr | 0.75mm | UL746 | 110 | °C |
1.5mm | UL746 | 115 | °C | |
Deflection Temperature Under Load? | 0.45MPa,Unannealed,4.00mm | ASTMD648 | >249 | °C |
0.45MPa,Unannealed | ISO75-2/B | 250 | °C | |
1.8MPa,Unannealed,4.00mm | ASTMD648 | >249 | °C | |
1.8MPa,Unannealed | ISO75-2/A | >240 | °C | |
Melting Temperature | ISO11357-3 | 263 | °C | |
Ball PressureTest | 253°C | IEC60695-10-2 | Pass |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Dielectric Constant | 23°C,50Hz | IEC60250 | 4.00 | |
23°C,1MHz | IEC60250 | 4.00 | ||
Surface Resistivity | IEC60093 | 1E+15 | ohms | |
Volume Resistivity | 23°C | IEC60093 | 1E+15 | ohms·cm |
Dissipation Factor? | 23°C,50Hz | IEC60250 | 0.012 | |
23°C,100Hz | IEC60250 | 0.012 | ||
23°C,1MHz | IEC60250 | 0.0190.019 | ||
Dielectric Strength | 23°C,1.00mm | IEC60243-1 | 35 | KV/mm |
23°C,3.00mm | IEC60243-1 | 30 | KV/mm | |
Relative Permittivity | 23°C,100Hz | IEC60250 | 4.00 | |
23°C,1MHz | IEC60250 | 4.00 | ||
Comparative Tracking Index | SolutionA | IEC60112 | 475 | V |
Film | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Film Puncture Energy | --7 | ISO6603-2 | 2.80 | J |
--8 | ISO6603-2 | 2.30 | J | |
Film Puncture Force | --7 | ISO6603-2 | 900 | N |
--8 | ISO6603-2 | 800 | N |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Notched Izod impact strength | -30°C | ISO180/1U | 55 | kJ/m² |
23°C | ISO180/1U | 60 | kJ/m² | |
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 60 | kJ/m² |
23°C | ISO179/1eU | 75 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Ball Indentation Hardness | ISO2039-1 | 220 | Mpa |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Oxygen Index | ISO4589-2 | 23 | % | |
BurningBehavior12 | >1.00mm | ISO3795 | passed | |
UL flame retardant rating | 0.75mm | UL94 | HB | |
1.5mm | UL94 | HB | ||
1.6mm | UL94 | HB | ||
3.0mm | UL94 | HB | ||
3.2mm | UL94 | HB | ||
Glow Wire Flammability Index | 0.8mm | IEC60695-2-12 | 700 | °C |
1.6mm | IEC60695-2-12 | 700 | °C | |
3.0mm | IEC60695-2-12 | 700 | °C |
Supplementary information | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
ISO Shortname | ISO1874 | PA66,GHR,14-100,GF30 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.