PA66 Leona™ FG173 NC ASAHI JAPAN

Unit Price:
$4396 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
145.9MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant Glass fiber reinforced Filler: Glass fiber reinf Glass fiber content is 30 Flame retardant grade UL9
Application Areas:Electrical field Electronic field Joint switch Hose Electrical/Electronic App Electrical components Joint switch switch Connector Other electrical and elec
Color:--
Grade:Enhanced level

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	干	旭化成方法	0.3-0.7	%
	Modeling Shrinkage	TD	内部方法	0.70	%
		Modeling Shrinkage	MD	内部方法	0.30	%
		Modeling Shrinkage	Modeling Shrinkage	吸水率(Saturation,23°C)	内部方法	--	%
Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	--	%
Taber Abrasion Resistance	湿	ASTM D-1044	29

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Modulus	干(湿)	ASTM D-790	10.8(8.3)	GPa
Tensile Stress	Break,23°C	ISO527-2	174	Mpa
Tensile Strain	Break,23°C	ISO527-2	2.0	%
Tensile Strength		ASTMD638	167	Mpa
Flexural Stress	23°C	ISO178	259	Mpa
Taber Abrasion Resistance	1000Cycles	ASTMD1044	--	mg
Tensile Strength	干(湿)	ASTM D-790	250(221)	Mpa
Elongation at break	干(湿)	ASTM D-638	2.5(2.7)	%
Notched Izod Impact Strength	干(湿)	ASTM D-256	88(98)	J/m
Tensile Modulus	23°C	ISO527-2	11700	Mpa
Tensile Strength	干(湿)	ASTM D-638	167(142)	Mpa
Tensile Elongation	Break	ASTMD638	2.5	%
Rockwell Hardness	干(湿)	ASTM D-785	100(60)	M Scale
Flexural Modulus		ASTMD790	10800	Mpa
Flexural Modulus	Flexural Modulus	23°C	ISO178	10300	Mpa
Flexural Strength		ASTMD790	250	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed	ASTMD648	260	°C
	Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	262	°C
		Deflection Temperature Under Load?	1.8MPa,Unannealed	ASTMD648	252	°C
			Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	245	°C
				Deflection Temperature Under Load?	1.82MPa,干	ASTM D-648	252	°C
				Deflection Temperature Under Load?	Deflection Temperature Under Load?	0.46MPa,干	ASTM D-648	260	°C
Linear expansion coefficient	干	ASTM D-696	3
Linear thermal expansion coefficient	MD	ASTMD696	3E-05	cm/cm/°C
Flame retardancy	干	UL 94	V-0

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength		ASTMD149	28	KV/mm
Dielectric Strength	Dielectric Strength		IEC60243-1	28	KV/mm
Comparative Tracking Index	3.00mm	IEC60112	275	V
Surface Resistivity		ASTMD257	1E+14	ohms
Surface Resistivity	Surface Resistivity		IEC60093	1E+14	ohms
Volume Resistivity		ASTMD257	1E+15	ohms·cm
Volume Resistivity	Volume Resistivity	23°C	IEC60093	1E+15	ohms·cm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength		ISO179	50	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Scale	ASTMD785	100
Rockwell Hardness	Rockwell Hardness	M-Scale	ISO2039-2	100

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	0.75mm	UL94	V-0
Glow Wire Flammability Index	3.0mm	IEC60695-2-12	960	°C

Physical	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	湿		0.6	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.