Material Description

Technical Data Sheet

Material Description

Material Properties:Thermal stability
Application Areas:Electrical applications Automotive interior parts
Color:--
Grade:Enhanced level

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Across Flow	ISO 294-4	0.80	%
Modeling Shrinkage	Modeling Shrinkage	流量	ISO 294-4	0.30	%
Moisture Absorption	24 hr, 23°C	ISO 62	0.83	%
	Moisture Absorption	Saturation, 23°C, 2.00 mm	ISO 62	4.5	%
	Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	1.5	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Stress	Break	ISO 527-2	142	Mpa
Tensile Strain	Break	ISO 527-2	4.0	%
Tensile Modulus		ISO 527-2	8700	Mpa
Flexural Modulus		ISO 178	7400	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45 MPa, Unannealed	ISO 75-2/B	262	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed	ISO 75-2/A	247	°C
Linear thermal expansion coefficient	Flow	ISO 11359-2	1.5E-5	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow	ISO 11359-2	1.2E-4	cm/cm/°C
Melting Temperature		ISO 11357-3	262	°C
Effective Thermal Diffusivity			8.50E-8	m²/s

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index		IEC 60112	--	V

Fill Analysis	Test Method	Test Result	Unit
Emission of Organic Compounds	VDA 277	25.0	µgC/g
Melt Density		1.12	g/cm³
Ejection Temperature		210	°C
Specific Heat Capacity of Melt		2200	J/kg/°C
Thermal Conductivity of Melt		0.22	W/m/K
Odor	VDA 270	3.00

Injection	Test Condition	Test Method	Test Result	Unit
Drying Temperature			80	°C
Drying time - Hot air dryer			2.0 到 4.0	hr
Suggested Max Moisture			0.20	%
Processing (Melt) Temp			285 到 305	°C
Melt Temperature, Optimum			295	°C
Mold Temperature			50 到 100	°C
Mold Temperature, Optimum			80	°C
Holding Pressure			50.0 到 100	Mpa
Holding Pressure	Holding Pressure	Drying Recommended		yes
Hold Pressure Time			3.00	s/mm
Maximum Screw Tangential Speed			12	m/min

Impact Properties	Test Condition	Test Method	Test Result	Unit
Notched Izod impact strength	-30°C	ISO 180/1U	80	kJ/m²
Notched Izod impact strength	Notched Izod impact strength	23°C	ISO 180/1U	74	kJ/m²
Charpy Unnotched Impact Strength	-30°C	ISO 179/1eU	80	kJ/m²
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO 179/1eU	91	kJ/m²

Flammability	Test Condition	Test Method	Test Result	Unit
Oxygen Index		ISO 4589-2	23	%
Burning Rate	1.00 mm	ISO 3795	23	mm/min
Flame Rating	0.75 mm	UL 94, IEC 60695-11-10, -20	HB
Flame Rating	Flame Rating	1.5 mm	UL 94, IEC 60695-11-10, -20	HB
FMVSS Flammability		FMVSS 302	SE/B
Haze		ISO 6452	8.0E-4	g

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.