PA66 Zytel® 80G33HSL-NC010 DUPONT USA
98
- Unit Price:
- $5342 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 55.1MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low temperature resistanc wear resistant
- Application Areas:Electronic and electrical Automotive components
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.85 | % |
| Saturation, 23°C, 2.00 mm | ISO 62 | 4.5 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | ISO 62 | 1.5 | % | |
| 24 hr, 23°C | ISO 62 | 0.91 | % | |
| Shrinkage rate | Across Flow | ISO 294-4 | 0.70 | % |
| 流量 | ISO 294-4 | 0.30 | % | |
| Stickiness number | 96% H2SO4 | ISO 307 | 144 | cm³/g |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile creep modulus | 1 hr | ISO 899-1 | -- | Mpa |
| 1000 hr | ISO 899-1 | -- | Mpa | |
| Bending stress | ISO 178 | 214 | Mpa | |
| Tensile stress | Break | ISO 527-2 | 148 | Mpa |
| Break | ISO 527-2 | 146 | Mpa | |
| Tensile strain | Break | ISO 527-2 | 3.7 | % |
| Break | ISO 527-2 | 3.6 | % | |
| Tensile modulus | ISO 527-2 | 8900 | Mpa | |
| ISO 527-2 | 8800 | Mpa | ||
| Bending modulus | ISO 178 | 7600 | Mpa | |
| ISO 178 | 7500 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 261 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 246 | °C | |
| 1.8 MPa, Unannealed | ISO 75-2/A | 245 | °C | |
| Vicat softening temperature | ISO 306/B50 | 245 | °C | |
| Linear coefficient of thermal expansion | Flow | ISO 11359-2 | 1.5E-5 | cm/cm/°C |
| Across Flow | ISO 11359-2 | 1.2E-4 | cm/cm/°C | |
| Flow | ISO 11359-2 | 2.4E-5 | cm/cm/°C | |
| Flow : -40 to 23°C | ISO 11359-2 | 2.5E-5 | cm/cm/°C | |
| Flow : 55 to 160°C | ISO 11359-2 | 9.0E-6 | cm/cm/°C | |
| Across Flow | ISO 11359-2 | 1.0E-4 | cm/cm/°C | |
| Across Flow : -40 to 23°C | ISO 11359-2 | 9.6E-5 | cm/cm/°C | |
| Across Flow : 55 to 160°C | ISO 11359-2 | 1.2E-4 | cm/cm/°C | |
| Effective Thermal Diffusivity | 9.00E-8 | m²/s | ||
| Glass transition temperature 3 | ISO 11357-2 | 75.0 | °C | |
| Melting temperature 3 | ISO 11357-3 | 262 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Leakage Trace Index | IEC 60112 | -- | V | |
| Surface resistivity | IEC 62631-3-2 | -- | ohms | |
| Volume resistivity | IEC 62631-3-1 | > 1.0E+13 | ohms·m |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Emission of Organic Compounds | VDA 277 | 25.3 | µgC/g | |
| VDA 277 | 25.0 | µgC/g | ||
| Melt density | 1.12 | g/cm³ | ||
| Top out temperature | 210 | °C | ||
| Specific Heat Capacity of Melt | 2200 | J/kg/°C | ||
| Thermal Conductivity of Melt | 0.22 | W/m/K | ||
| Odor | VDA 270 | 3.00 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 80 | °C | ||
| Drying time - hot air dryer | 2.0 到 4.0 | hr | ||
| Suggested maximum moisture content | 0.20 | % | ||
| Processing (melt) temperature | 285 到 305 | °C | ||
| Melt Temperature, Optimum | 295 | °C | ||
| Mold temperature | 50 到 100 | °C | ||
| Mold Temperature, Optimum | 80 | °C | ||
| Maintain pressure | 50.0 到 100 | Mpa | ||
| Drying Recommended | yes | |||
| Hold Pressure Time | 3.00 | s/mm | ||
| Maximum Screw Tangential Speed | 12 | m/min |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 110 | kJ/m² |
| 23°C | ISO 179/1eU | 97 | kJ/m² | |
| -40°C | ISO 179/1eU | 110 | kJ/m² | |
| Unscented Izod impact strength | -30°C | ISO 180/1U | 80 | kJ/m² |
| 23°C | ISO 180/1U | 80 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M -Sale | ISO 2039-2 | 70 | |
| R -Sale | ISO 2039-2 | 110 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning rate | 1.00 mm | ISO 3795 | 23 | mm/min |
| UL flame retardant rating | 0.75 mm | UL 94, IEC 60695-11-10, -20 | HB | |
| 1.5 mm | UL 94, IEC 60695-11-10, -20 | HB | ||
| FMVSS flammability | FMVSS 302 | SE/B | ||
| 雾化 - G-value (condensate) | ISO 6452 | 8.0E-4 | g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.