Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD：1.00mm3 | % | 0.40到0.80 | -- |
| Modeling Shrinkage | MD：3.00mm4 | % | 1.0到1.3 | -- |
| Moisture Absorption | 23°C,24hr | % | 1.7 | -- |
| Moisture Absorption | Saturation,23°C | % | 9.5 | -- |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | 23°C | MPa | 80.0 | 45.0 |
| Tensile Stress | 80°C | MPa | 40.0 | -- |
| Tensile Strain | Break,23°C | % | 7.5 | 37 |
| Tensile Strain | Break,80°C | % | 56 | -- |
| Flexural Modulus | 23°C | MPa | 3500 | 1200 |
| Flexural Modulus | 80°C | MPa | 1000 | -- |
| Flexural Stress | -40°C | MPa | 150 | -- |
| Flexural Stress | 23°C | MPa | 115 | 45.0 |
| Flexural Stress | 80°C | MPa | 55.0 | -- |
| Taber Abrasion Resistance | 1000Cycles | mg | 5.00到6.00 | -- |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | °C | 207 | -- |
| Melting temperature | | °C | 225 | -- |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume Resistivity | | ohms·cm | 1E+15 | -- |
| Dielectric Strength | | kV/mm | 30 | -- |
| Comparative Tracking Index | CTI | V | 600 | -- |
| Dielectric Constant | 23°C,1MHz | | 5.20 | -- |
| Dissipation Factor | 23°C,1MHz | | 0.080 | -- |
| Arc Resistance | | sec | 120 | -- |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R-Sale,23°C | | 120 | -- |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.79mm | | V-0 | -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.