PA66 Leona™ 14G50 BK ASAHI JAPAN

135

Unit Price:
$4408 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Creep resistance Moderate heat resistance Thermal stability Fatigue resistance high strength High rigidity Filler: Glass fiber reinf 50% filler by weight
Application Areas:Bar stock Electrical field Electronic field component Automotive sector Bar stock Electrical/Electronic App Engine mount component Mechanical and electrical Application in the automo And other parts under the
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	干	旭化成方法	0.4/0.7	%
	Modeling Shrinkage	TD	内部方法	0.70	%
		Modeling Shrinkage	MD	内部方法	0.40	%
		Modeling Shrinkage	Modeling Shrinkage	吸水率(Saturation,23°C)	内部方法	--	%
Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	--	%
Taber Abrasion Resistance	湿	ASTM D-1044	22	×10-6kg/1000times

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Modulus	干(湿)	ASTM D-790	14.5(9.8)	GPa
Notched Izod Impact Strength	干(湿)	ASTM D-256	140(190)	J/m
Tensile Stress	Break,23°C	ISO527-2	237	Mpa
Tensile Strain	Break,23°C	ISO527-2	2.0	%
Tensile Strength		ASTMD638	235	Mpa
Flexural Stress	23°C	ISO178	371	Mpa
Taber Abrasion Resistance	1000Cycles	ASTMD1044	--	mg
Tensile Strength	干(湿)	ASTM D-790	390(280)	Mpa
Elongation at break	干(湿)	ASTM D-638	2.5(4)	%
Tensile Modulus	23°C	ISO527-2	16900	Mpa
Tensile Strength	干(湿)	ASTM D-638	235(170)	Mpa
Tensile Elongation	Break	ASTMD638	2.5	%
Rockwell Hardness	干(湿)	ASTM D-785	95(80)	M Scale
Rockwell Hardness	Rockwell Hardness	干(湿)	ASTM D-785	118(-)	R scale
Flexural Modulus		ASTMD790	14500	Mpa
Flexural Modulus	Flexural Modulus	23°C	ISO178	13600	Mpa
Flexural Strength		ASTMD790	390	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed	ASTMD648	260	°C
	Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	260	°C
		Deflection Temperature Under Load?	1.8MPa,Unannealed	ASTMD648	250	°C
			Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	255	°C
				Deflection Temperature Under Load?	1.82MPa,干	ASTM D-648	250	°C
				Deflection Temperature Under Load?	Deflection Temperature Under Load?	0.46MPa,干	ASTM D-648	260	°C
Linear expansion coefficient	干	ASTM D-696	2	×10-5/K
Thermal Conductivity	干		0.4	W/(m.K)
Linear thermal expansion coefficient	MD	ASTMD696	2E-05	cm/cm/°C
Flame retardancy	干	UL 94	HB
Thermal Conductivity			0.40	W/m/K

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength		ASTMD149	21	KV/mm
Dielectric Strength	Dielectric Strength		IEC60243-1	21	KV/mm
Comparative Tracking Index	3.00mm	IEC60112	525	V
Surface Resistivity		ASTMD257	1E+15	ohms
Surface Resistivity	Surface Resistivity		IEC60093	1E+15	ohms
Volume Resistivity		ASTMD257	1E+15	ohms·cm
Volume Resistivity	Volume Resistivity	23°C	IEC60093	1E+15	ohms·cm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength		ISO179	NoBreak

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Sale	ASTMD785	95
	Rockwell Hardness	R-Sale	ASTMD785	118
		Rockwell Hardness	M-Sale	ISO2039-2	95
		Rockwell Hardness	Rockwell Hardness	R-Sale	ISO2039-2	118

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	0.75mm	UL94	HB

Physical	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	湿		1.3	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.