PA66 Zytel® 70G43HSL BK099 DUPONT KOREA

Unit Price:
$3446 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
21.1MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Across Flow	ISO 294-4	0.90	%
Modeling Shrinkage	Modeling Shrinkage	流量	ISO 294-4	0.30	%
Moisture Absorption	24 hr, 23°C, 2.00 mm	ISO 62	0.90	%
	Moisture Absorption	Saturation, 23°C, 2.00 mm	ISO 62	4.7	%
	Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	1.5	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Stress	Break	ISO 527-2	225	Mpa
Tensile Strain	Break	ISO 527-2	2.5	%
Tensile Modulus		ISO 527-2	14000	Mpa
Flexural Modulus		ISO 178	12500	Mpa
Flexural Stress		ISO 178	340	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Glass Transition Temperature		ISO 11357-2	80.0	°C
Melting Temperature		ISO 11357-3	262	°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed	ISO 75-2/B	258	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed	ISO 75-2/A	255	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume Resistivity		IEC 62631-3-1	> 1.0E+13	ohms·m
Dissipation Factor?	100 Hz	IEC 62631-2-1	0.013
Dissipation Factor?	Dissipation Factor?	1 MHz	IEC 62631-2-1	0.015
Dielectric Strength		IEC 60243-1	25	KV/mm
Comparative Tracking Index		IEC 60112	600	V

Fill Analysis	Test Condition	Test Method	Test Result	Unit
Ejection Temperature			210	°C
Thermal Conductivity of Melt			0.25	W/m/K

Injection	Test Condition	Test Method	Test Result	Unit
Drying Temperature			80	°C
Drying time - Hot air dryer			2.0 到 4.0	hr
Suggested Max Moisture			0.20	%
Processing (Melt) Temp			285 到 300	°C
Melt Temperature, Optimum			295	°C
Mold Temperature			70 到 120	°C
Mold Temperature, Optimum			100	°C
Holding Pressure			50.0 到 100	Mpa
Holding Pressure	Holding Pressure	Drying Recommended		yes
Hold Pressure Time			3.00	s/mm
Maximum Screw Tangential Speed			12	m/min

Impact Properties	Test Condition	Test Method	Test Result	Unit
Multi-Axial Instrumented Impact Energy	23°C	ISO 6603-2	4.40	J
Charpy Unnotched Impact Strength	23°C	ISO 179/1eU	90	kJ/m²

Flammability	Test Condition	Test Method	Test Result	Unit
Burning Rate	1.00 mm	ISO 3795	27	mm/min
FMVSS Flammability		FMVSS 302	B
Oxygen Index		ISO 4589-2	24	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.