PA66 Zytel® 70G50HSLA BK039B DUPONT USA
92
- Unit Price:
- $3769 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 81.6MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Dimensional stability
- Application Areas:Electrical tools Electrical applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ASTM D792/ISO 1183 | 1.57 |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD | ISO294-4 | 0.80 | % |
| MD | ISO294-4 | 0.30 | % | |
| Moisture Absorption | Saturation,23°C,2.00mm | ISO62 | 4.2 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 1.2 | % | |
| MediumDensity | 1.40 | g/cm³ | ||
| Ejection Temperature | 210 | °C | ||
| SpecificHeatCapacityofMelt | 1870 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.31 | W/m/K |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Stress | ISO178 | 400 | Mpa | |
| Tensile Stress | Break | ISO527-2 | 250 | Mpa |
| Tensile Strain | Break | ISO527-2 | 2.4 | % |
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | 2.2 | % | |
| Tensile Modulus | ASTM D638/ISO 527 | 16800 | kg/cm²(MPa)[Lb/in²] | |
| ISO527-2 | 17000 | Mpa | ||
| Tensile Strength | ASTM D638/ISO 527 | 245 | kg/cm²(MPa)[Lb/in²] | |
| Flexural Modulus | ISO178 | 16000 | Mpa | |
| Charpy impact strength | ASTM D256/ISO 179 | 16 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 95 | kg·cm/cm(J/M)ft·lb/in |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear thermal expansion coefficient | MD：-- | ISO11359-2 | 9E-06 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 1.9E-05 | cm/cm/°C | |
| MD：55to160°C | ISO11359-2 | 8E-06 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 7.2E-05 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 5.8E-05 | cm/cm/°C | |
| TD：55to160°C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| TD：导热系数 | ISO11359-2 | 0.46 | W/m/K | |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 261 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 255 | °C | |
| ASTM D648/ISO 75 | 253 | ℃（℉） | ||
| Melting Temperature | 262 | ℃（℉） | ||
| Melting Temperature | ISO11357-3 | 262 | °C | |
| Vicat Softening Temperature | ISO306/B50 | 255 | °C | |
| Glass Transition Temperature | ISO11357-2 | 80.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume Resistivity | IEC60093 | 1E+15 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Multi-Axial Instrumented Impact Energy | 23°C | ISO6603-2 | 10.0 | J |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 90 | kJ/m² |
| 23°C | ISO179/1eU | 100 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.8mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| Oxygen Index | ISO4589-2 | 24 | % | |
| FMVSS Flammability | FMVSS302 | SE | ||
| Fogging-G-value | condensate | ISO6452 | 4E-04 | g |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 6.50 | µgC/g | |
| Odor | VDA270 | 3.00 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.