PA66 Leona™ 90G60 ASAHI JAPAN
93
- Unit Price:
- $3815 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 39.3MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High rigidity
- Application Areas:Automotive External Parts
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Modeling Shrinkage | TD | 内部方法 | 0.50 | % |
MD | 内部方法 | 0.20 | % | |
干 | 旭化成方法 | 0.2/0.5 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Tensile Stress | Break,23°C | ISO527-2 | 189 | Mpa |
Tensile Strain | Break,23°C | ISO527-2 | 2.0 | % |
Tensile Strength | ASTMD638 | 190 | Mpa | |
Flexural Stress | 23°C | ISO178 | 324 | Mpa |
Tensile Modulus | 23°C | ISO527-2 | 18200 | Mpa |
Tensile Strength | 干(湿) | ASTM D-638 | 190(148) | Mpa |
Tensile Elongation | Break | ASTMD638 | 2.0 | % |
Rockwell Hardness | 干(湿) | ASTM D-785 | 95(88) | M Scale |
干(湿) | ASTM D-785 | 120(117) | R scale | |
Flexural Modulus | ASTMD790 | 16000 | Mpa | |
23°C | ISO178 | 15800 | Mpa | |
Flexural Strength | ASTMD790 | 300 | Mpa | |
Tensile Strength | 干(湿) | ASTM D-790 | 300(234) | Mpa |
Elongation at break | 干(湿) | ASTM D-638 | 2(3) | % |
Notched Izod Impact Strength | 干(湿) | ASTM D-256 | 95(100) | J/m |
Flexural Modulus | 干(湿) | ASTM D-790 | 16.0(12.9) | GPa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Thermal Conductivity | 干 | 0.3 | W/(m.K) | |
Specific Heat | 干 | 1840 | J/(kg.k) | |
Specific Heat | 1840 | J/kg/°C | ||
Thermal Conductivity | 0.30 | W/m/K | ||
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 210 | °C |
1.82MPa,干 | ASTM D-648 | 225 | °C | |
0.45MPa,Unannealed | ISO75-2/B | 230 | °C | |
1.8MPa,Unannealed | ASTMD648 | 225 | °C | |
Linear expansion coefficient | 干 | ASTM D-696 | 2 | |
Linear thermal expansion coefficient | MD | ASTMD696 | 2E-05 | cm/cm/°C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Dielectric Strength | ASTMD149 | 28 | KV/mm | |
IEC60243-1 | 28 | KV/mm | ||
Surface Resistivity | ASTMD257 | 1E+13 | ohms | |
IEC60093 | 1E+13 | ohms | ||
Comparative Tracking Index | 3.00mm | IEC60112 | 475 | V |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Charpy Unnotched Impact Strength | ISO179 | 56 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Rockwell Hardness | M-Sale | ASTMD785 | 95 | |
R-Sale | ASTMD785 | 120 | ||
M-Sale | ISO2039-2 | 95 | ||
R-Sale | ISO2039-2 | 120 |
Physical | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Moisture Absorption | 湿 | 0.9 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.