PA66 Leona™ 13G25 ASAHI JAPAN

Unit Price:
$3498 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
47MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD	内部方法	0.90	%
	Modeling Shrinkage	MD	内部方法	0.50	%
	Modeling Shrinkage	Modeling Shrinkage	干	旭化成方法	0.5/0.9	%
Taber Abrasion Resistance	湿	ASTM D-1044	12	×10-6kg/1000times

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Modulus	干(湿)	ASTM D-790	8.1(4.7)	GPa
Tensile Stress	Break,23°C	ISO527-2	190	Mpa
Tensile Strain	Break,23°C	ISO527-2	4.0	%
Tensile Strength		ASTMD638	180	Mpa
Flexural Stress	23°C	ISO178	275	Mpa
Tensile Strength	干(湿)	ASTM D-790	290(175)	Mpa
Elongation at break	干(湿)	ASTM D-638	3(6)	%
Notched Izod Impact Strength	干(湿)	ASTM D-256	105(160)	J/m
Tensile Modulus	23°C	ISO527-2	8200	Mpa
Tensile Strength	干(湿)	ASTM D-638	180(110)	Mpa
Tensile Elongation	Break	ASTMD638	3.0	%
Rockwell Hardness	干(湿)	ASTM D-785	96(74)	M Scale
Rockwell Hardness	Rockwell Hardness	干(湿)	ASTM D-785	120(-)	R scale
Flexural Modulus		ASTMD790	8100	Mpa
Flexural Modulus	Flexural Modulus	23°C	ISO178	7800	Mpa
Flexural Strength		ASTMD790	290	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed	ASTMD648	260	°C
	Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	260	°C
		Deflection Temperature Under Load?	1.8MPa,Unannealed	ASTMD648	250	°C
			Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	245	°C
				Deflection Temperature Under Load?	0.46MPa,干	ASTM D-648	260	°C
				Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.82MPa,干	ASTM D-648	250	°C
Linear expansion coefficient	干	ASTM D-696	3	×10-5/K
Thermal Conductivity	干		0.3	W/(m.K)
Linear thermal expansion coefficient	MD	ASTMD696	3E-05	cm/cm/°C
Flame retardancy	干	UL 94	HB
Thermal Conductivity			0.30	W/m/K

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index	3.00mm	IEC60112	600	V
Dielectric Strength		ASTMD149	29	KV/mm
Dielectric Strength	Dielectric Strength		IEC60243-1	29	KV/mm
Surface Resistivity		ASTMD257	1E+15	ohms
Surface Resistivity	Surface Resistivity		IEC60093	1E+15	ohms
Volume Resistivity		ASTMD257	1E+15	ohms·cm
Volume Resistivity	Volume Resistivity	23°C	IEC60093	1E+15	ohms·cm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength		ISO179	68	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Sale	ASTMD785	96
	Rockwell Hardness	R-Sale	ASTMD785	120
		Rockwell Hardness	M-Sale	ISO2039-2	96
		Rockwell Hardness	Rockwell Hardness	R-Sale	ISO2039-2	120

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	0.75mm	UL94	HB

Physical	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	湿		1.9	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.