PA66 Leona™ 1330G ASAHI JAPAN

Unit Price:
$4586 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
53.7MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Lubricity Low friction coefficient high strength
Application Areas:Engine hood parts Industrial applications component Automotive sector
Color:--
Grade:Enhanced level

Technical Data Sheet

Physical Properties	Test Method	Test Result	Unit
Density	ASTM D792/ISO 1183	1.48
Modeling Shrinkage	ASTM D955	0.5-1.0	%
Moisture Absorption 23℃/24H	ASTM D570/ISO 62	1.4	%

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD	内部方法	1.0	%
	Modeling Shrinkage	MD	内部方法	0.50	%
	Modeling Shrinkage	Modeling Shrinkage	干	旭化成方法	0.5-1.0	%
Taber Abrasion Resistance	湿	ASTM D-1044	9	×10-6kg/1000times

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Modulus	干(湿)	ASTM D-790	8.0(6.3)	GPa
Flexural Stress	23°C	ISO178	235	Mpa
Tensile Strength	干(湿)	ASTM D-790	245(177)	Mpa
Elongation at break	干(湿)	ASTM D-638	3(3)	%
Notched Izod Impact Strength	干(湿)	ASTM D-256	98(118)	J/m
Tensile Strength		ASTMD638	157	Mpa
Tensile Modulus	23°C	ISO527-2	9800	Mpa
Tensile Strength	干(湿)	ASTM D-638	157(118)	Mpa
Tensile Elongation	Break	ASTMD638	3.0	%
Rockwell Hardness	干(湿)	ASTM D-785	89(60)	M Scale
	Rockwell Hardness		ASTM D785	R120
	Rockwell Hardness	Rockwell Hardness	干(湿)	ASTM D-785	120(108)	R scale
Flexural Modulus		ASTM D790/ISO 178	8040(MPa)	kg·cm/cm(J/M)ft·lb/in
	Flexural Modulus		ASTMD790	8000	Mpa
	Flexural Modulus	Flexural Modulus	23°C	ISO178	8700	Mpa
Flexural Strength		ASTMD790	245	Mpa
Flexural Strength	Flexural Strength		ASTM D790/ISO 178	245(MPa)	kg·cm/cm(J/M)ft·lb/in
Tensile Stress	Break,23°C	ISO527-2	144	Mpa
Tensile Strain	Break,23°C	ISO527-2	4.0	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Linear thermal expansion coefficient	MD	ASTMD696	3E-05	cm/cm/°C
Burning Rate		UL94	HB
Deflection Temperature Under Load?		ASTM D648/ISO 75	248	℃（℉）
	Deflection Temperature Under Load?	1.8MPa,Unannealed	ASTMD648	248	°C
		Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	246	°C
			Deflection Temperature Under Load?	0.46MPa,干	ASTM D-648	260	°C
				Deflection Temperature Under Load?	1.82MPa,干	ASTM D-648	248	°C
					Deflection Temperature Under Load?	0.45MPa,Unannealed	ASTMD648	260	°C
					Deflection Temperature Under Load?	Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	261	°C
Linear expansion coefficient	干	ASTM D-696	3	×10-5/K
Flame retardancy	干	UL 94	HB

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength		ISO179	71	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Sale	ASTMD785	89
	Rockwell Hardness	R-Sale	ASTMD785	120
		Rockwell Hardness	M-Sale	ISO2039-2	89
		Rockwell Hardness	Rockwell Hardness	R-Sale	ISO2039-2	120

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	0.75mm	UL94	HB

Physical	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	湿		1.4	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.