Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.52 | |
Modeling Shrinkage | | ASTM D955 | 0.5-1.0 | % |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 1.4 | % |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | 干 | 旭化成方法 | 0.5-1.0 | % |
Modeling Shrinkage | MD | ASTMD995 | 0.50 | % |
Modeling Shrinkage | TD | ASTMD995 | 1.0 | % |
Moisture Absorption | (23°C,50RH) | ASTMD570 | 1.4 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength | 干(湿) | ASTM D-790 | 191(157) | Mpa |
Elongation at break | 干(湿) | ASTM D-638 | 3(3.5) | % |
Notched Izod Impact Strength | 干(湿) | ASTM D-256 | 36(39) | J/m |
Tensile Elongation?(Break) | 23°C | ASTMD638 | 3.0 | % |
Tensile Strength | Yield,23°C | ASTMD638 | 128 | Mpa |
Tensile Strength | 干(湿) | ASTM D-638 | 128(98) | Mpa |
Rockwell Hardness | 干(湿) | ASTM D-785 | 90(-) | R scale |
Rockwell Hardness | | ASTM D785 | M90 | |
Flexural Modulus | | ASTM D790/ISO 178 | 8830(MPa) | kg·cm/cm(J/M)ft·lb/in |
Flexural Modulus | 23°C | ASTMD790 | 8800 | Mpa |
Flexural Strength | 23°C | ASTMD790 | 191 | Mpa |
Flexural Strength | | ASTM D790/ISO 178 | 191(MPa) | kg·cm/cm(J/M)ft·lb/in |
Notched Izod Impact Strength | 23°C | ASTMD256 | 36.0 | J/m |
Flexural Modulus | 干(湿) | ASTM D-790 | 8.8(5.8) | GPa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Burning Rate | | UL94 | HB | |
Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 245 | ℃(℉) |
Deflection Temperature Under Load? | 1.82MPa,干 | ASTM D-648 | 245 | °C |
Deflection Temperature Under Load? | 0.46MPa,干 | ASTM D-648 | 250 | °C |
Deflection Temperature Under Load? | 0.45MPaUnannealed | ASTMD648 | 250 | °C |
Deflection Temperature Under Load? | 1.80MPaUnannealed | ASTMD648 | 245 | °C |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | | ASTMD785 | 90 | M(Scale) |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | 湿 | | 1.4 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.