PA66 Leona™ CR301 ASAHI JAPAN

Unit Price:
$4480 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
42.7MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:dimensional stability Conductive
Application Areas:Electrical field Electrical components Electronic field Industrial applications Switch panel
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Method	Test Result	Unit
Density	ASTM D792/ISO 1183	1.48
Modeling Shrinkage	ASTM D955	0.5-1.3	%
Moisture Absorption 23℃/24H	ASTM D570/ISO 62	1.5	%

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	干	旭化成方法	0.5-1.3	%
Moisture Absorption	Saturation, 23°C		--	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	--	%
Taber Abrasion Resistance	湿	ASTM D-1044	8	×10-6kg/1000times
Modeling Shrinkage (Flow)		内部方法	0.50 到 1.3	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Modulus	干(湿)	ASTM D-790	5.9(2.9)	GPa
Taber Abrasion Resistance	1000 Cycles	ASTM D1044	--	mg
Tensile Strength	干(湿)	ASTM D-790	147(93)	Mpa
Elongation at break	干(湿)	ASTM D-638	3(3.5)	%
Notched Izod Impact Strength	干(湿)	ASTM D-256	34(39)	J/m
Tensile Stress	Break, 23°C	ISO 527-2	85.0	Mpa
Tensile Stress	Tensile Stress	--	ASTM D638	88.0	Mpa
Tensile Modulus	23°C	ISO 527-2	7000	Mpa
Tensile Strength	干(湿)	ASTM D-638	88(64)	Mpa
Tensile Elongation	Break	ASTM D638	3.0	%
Tensile Elongation	Tensile Elongation	Break, 23°C	ISO 527-2	2.0	%
Rockwell Hardness	干(湿)	ASTM D-785	85(-)	M Scale
Rockwell Hardness	Rockwell Hardness		ASTM D785	M85
Flexural Modulus		ASTM D790/ISO 178	5880(MPa)	kg·cm/cm(J/M)ft·lb/in
	Flexural Modulus	--	ASTM D790	5900	Mpa
	Flexural Modulus	Flexural Modulus	23°C	ISO 178	7400	Mpa
Flexural Strength	--	ASTM D790	147	Mpa
	Flexural Strength	23°C	ISO 178	140	Mpa
	Flexural Strength	Flexural Strength		ASTM D790/ISO 178	147(MPa)	kg·cm/cm(J/M)ft·lb/in

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Burning Rate		UL94	HB
Deflection Temperature Under Load?		ASTM D648/ISO 75	191	℃（℉）
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.82MPa,干	ASTM D-648	191(250)	°C
Linear expansion coefficient	干	ASTM D-696	4	×10-5/K
Linear expansion coefficient	Linear expansion coefficient		ASTM D696/ISO 11359	4	mm/mm.℃
Deflection Temperature Under Load?	0.45 MPa, Unannealed	ASTM D648	250	°C
	Deflection Temperature Under Load?	0.45 MPa, Unannealed	ISO 75-2/B	249	°C
		Deflection Temperature Under Load?	1.8 MPa, Unannealed	ASTM D648	191	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed	ISO 75-2/A	188	°C
Coefficient of Linear Thermal Expansion (Flow)		ASTM D696	4.0E-5	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Arc Resistance		ASTM D495/IEC 60112	150

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength		ISO 179	51	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Scale	ASTM D785	85
Rockwell Hardness	Rockwell Hardness	M -Sale	ISO 2039-2	85

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	0.75 mm	UL 94	HB

Physical	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	湿		1.5	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.