PA6 BKV30H2.0 901510 LANXESS WUXI
66
- Unit Price:
- $2974 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:30% glass fiber reinforce Easy to flow Thermal stability rating
- Application Areas:--
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | 1mm/min | ISO 527-1,-2 | 9000 | Mpa |
| Tensile Strength | 5mm/min | ISO 527-1,-2 | 170 | Mpa |
| Flexural Modulus | 2mm/min | ISO 178 | 8000 | Mpa |
| Flexural Strength | 2mm/min | ISO 178 | 260 | Mpa |
| Charpy Notched Impact Strength | -30℃ | ISO 179-1eA | ＜10 | kJ/m² |
| 3.5%应变下的弯曲应力 | 2mm/min | ISO 178 | 250 | Mpa |
| Tensile Strain | 2mm/min | ISO 178 | 4.1 | % |
| Elongation at break | 5mm/min | ISO 527-1,-2 | 3.2 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load | 8.00MPa | ISO 75-1,-2 | 150 | °C |
| Deflection Temperature Under Load | 1.80MPa | ISO 75-1,-2 | 200 | °C |
| Processing | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Temperature | ISO 294 | 280 | °C | |
| Mold Temperature | ISO 294 | 80 | °C | |
| Injection Rate | ISO 294 | 200 | mm/s |
| Other | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Filler Content | ISO 3451-1 | 30 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.