PA6 6I3 NC DOMO CHEM GERMANY

Unit Price:
$3945 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:--

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Across Flow : 23°C, 72hr	ISO 2577	1.6 到 1.8	%
Modeling Shrinkage	Modeling Shrinkage	流量 : 23°C, 72hr	ISO 2577	1.2 到 1.4	%
Viscosity number	96% H2SO4	ISO 307	145	cm³/g

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Stress	Yield	ISO 527-2/50	60.0	Mpa
Tensile Strain	Break	ISO 527-2/50	> 50	%
Tensile Modulus		ISO 527-2/1	2200	Mpa
Flexural Modulus		ISO 178	2000	Mpa
Flexural Stress		ISO 178	75.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Melting temperature		ISO 11357-3	221	°C
Vicat Softening Temperature		ISO 306/B50	175	°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed	ISO 75-2/B	140	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed	ISO 75-2/A	55.0	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface Resistivity		IEC 60093	1.0E+13	ohms
Volume Resistivity		IEC 60093	1.0E+15	ohms·cm

Injection	Test Result	Unit
Drying Temperature	75 到 85	°C
Processing (Melt) Temp	240 到 260	°C
Mold Temperature	60 到 90	°C
Drying Time	2.0 到 4.0	hr

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-30°C	ISO 179/1eU	无断裂
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO 179/1eU	无断裂
Notched Izod impact strength	23°C	ISO 180/1U	无断裂

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R -Sale	ISO 2039-2	102

Flammability	Test Condition	Test Method	Test Result	Unit
Burning Rate		FMVSS 302	< 100	mm/min
Flame Rating	0.8 mm	UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.