Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD:3.18mm | | 0.30 | % |
Moisture Absorption | 24hr | ASTMD570 | 1.1 | % |
Moisture Absorption | 23°C,24hr | ISO62 | 1.1 | % |
Moisture Absorption | Saturation | ASTMD570 | 6.4 | % |
Moisture Absorption | Saturation,23°C | ISO62 | 6.4 | % |
Moisture Absorption | Equilibrium,50%RH | ASTMD570 | 1.8 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 1.8 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Elongation | Break,23°C | ASTMD638 | 3.0 | % |
Flexural Modulus | 23°C | ASTMD790 | 9380 | Mpa |
Flexural Modulus | 23°C | ISO178 | 8400 | Mpa |
Flexural Strength | 23°C | ASTMD790 | 265 | Mpa |
Tensile Stress | Break,23°C | ISO527-2 | 175 | Mpa |
Tensile Strain | Break,23°C | ISO527-2 | 3.0 | % |
Tensile Strength | Break,23°C | ASTMD638 | 175 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
RTIElec | 6.0mm | UL746 | 140 | °C |
RTIElec | 0.71mm | UL746 | 130 | °C |
RTIElec | 1.5mm | UL746 | 140 | °C |
RTIElec | 3.0mm | UL746 | 140 | °C |
Evolution Calendar intelligent importer | 0.71mm | UL746 | 115 | °C |
Evolution Calendar intelligent importer | 1.5mm | UL746 | 115 | °C |
Evolution Calendar intelligent importer | 3.0mm | UL746 | 120 | °C |
Evolution Calendar intelligent importer | 6.0mm | UL746 | 120 | °C |
RTIStr | 0.71mm | UL746 | 140 | °C |
RTIStr | 1.5mm | UL746 | 140 | °C |
RTIStr | 3.0mm | UL746 | 140 | °C |
RTIStr | 6.0mm | UL746 | 140 | °C |
Linear thermal expansion coefficient | MD | ASTME831 | 3.8E-05 | cm/cm/°C |
Peak Melting Temperature | | ASTMD3418 | 220 | °C |
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 174 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ASTMD648 | 208 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 54.0 | °C |
Melting temperature (DSC) | | ISO3146 | 220 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Volume Resistivity | | IEC60093 | >1.0E+13 | ohms·cm |
Volume Resistivity | 1.50mm | ASTMD257 | >1.0E+13 | ohms·cm |
Dielectric Strength | 1.50mm | ASTMD149 | 22 | KV/mm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Drop Impact Resistance | 23°C | 内部方法 | 4.61 | J |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Scale | ASTMD785 | 120 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.5mm | UL94 | HB | |
UL flame retardant rating | 3.0mm | UL94 | HB | |
UL flame retardant rating | 6.0mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.