Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD:280°C,2.00mm2 | ISO294-4 | 0.70 | % |
| Modeling Shrinkage | TD:120°C,2hr,2.00mm3 | ISO294-4 | 0.14 | % |
| Modeling Shrinkage | MD:280°C,2.00mm2 | ISO294-4 | 0.23 | % |
| Modeling Shrinkage | MD:120°C,2hr,2.00mm3 | ISO294-4 | 0.070 | % |
| Moisture Absorption | Saturation,23°C | ISO62 | 6.5 | % |
| Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 1.9 | % |
| Apparent Density | | ISO60 | 0.70 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | Break,23°C | ISO527-2/5 | 180 | Mpa |
| Tensile Strain | Break,23°C | ISO527-2/5 | 3.0 | % |
| Tensile Creep Modulus | 1000hr | ISO899-1 | -- | Mpa |
| Tensile Modulus | 23°C | ISO527-2/1 | 10700 | Mpa |
| Tensile Creep Modulus | 1hr | ISO899-1 | -- | Mpa |
| Flexural Stress | 3.5%Strain | ISO178/A | 280 | Mpa |
| Flexural Stress | 23°C | ISO178 | 290 | Mpa |
| Flexural Stress | FlexuralStrainatFlexuralStrength5(23°C) | | 4.0 | % |
| Flexural Modulus | 23°C | ISO178/A | 10700 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear thermal expansion coefficient | MD：23to55°C | ISO11359-2 | 2E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | TD：23to55°C | ISO11359-2 | 8E-05 | cm/cm/°C |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 215 | °C |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 205 | °C |
| Deflection Temperature Under Load? | 8.0MPa,Unannealed | ISO75-2/C | 150 | °C |
| Vicat Softening Temperature | -- | ISO306/B50 | 200 | °C |
| Vicat Softening Temperature | -- | ISO306/B120 | >200 | °C |
| Melting Temperature | | ISO11357-3 | 222 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation Factor? | 23°C,100Hz | IEC60250 | 7E-03 | |
| Dissipation Factor? | 23°C,1MHz | IEC60250 | 0.015 | |
| Surface Resistivity | | IEC60093 | 1E+14 | ohms |
| Volume Resistivity | 23°C | IEC60093 | 1E+15 | ohms·cm |
| Dielectric Strength | 23°C,1.00mm | IEC60243-1 | 40 | KV/mm |
| Relative Permittivity | 23°C,100Hz | IEC60250 | 4.00 | |
| Relative Permittivity | 23°C,1MHz | IEC60250 | 4.00 | |
| Comparative Tracking Index | SolutionA | IEC60112 | 525 | V |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|
| Film Puncture Energy | --6 | ISO6603-2 | 3.30 | J |
| Film Puncture Energy | --7 | ISO6603-2 | 3.90 | J |
| Film Puncture Force | --6 | ISO6603-2 | 945 | N |
| Film Puncture Force | --7 | ISO6603-2 | 1060 | N |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod impact strength | -30°C | ISO180/1U | 70 | kJ/m² |
| Notched Izod impact strength | 23°C | ISO180/1U | 75 | kJ/m² |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 70 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 80 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball Indentation Hardness | | ISO2039-1 | 230 | Mpa |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.6mm | UL94 | HB | |
| UL flame retardant rating | 3.2mm | UL94 | HB | |
| Glow Wire Flammability Index | 2.0mm | IEC60695-2-12 | 650 | °C |
| Oxygen Index | | ISO4589-2 | 23 | % |
| BurningBehavior10 | >1.00mm | ISO3795 | passed | |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|
| ISO Shortname | | ISO1874 | PA6,GR,14-110,GF35 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.