Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD | ISO294-4 | 0.70 | % |
Modeling Shrinkage | MD | ISO294-4 | 0.20 | % |
Moisture Absorption | Saturation,23°C,2.00mm | ISO62 | 2.0 | % |
MediumDensity | | | 1.24 | g/cm³ |
Ejection Temperature | | | 150 | °C |
SpecificHeatCapacityofMelt | | | 2100 | J/kg/°C |
ThermalConductivityofMelt | | | 0.28 | W/m/K |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Break | ISO527-2 | 200 | Mpa |
Tensile Strain | Break | ISO527-2 | 3.5 | % |
Tensile Modulus | | ISO527-2 | 12000 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 220 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 212 | °C |
Linear thermal expansion coefficient | MD | ISO11359-2 | 7E-06 | cm/cm/°C |
Linear thermal expansion coefficient | TD | ISO11359-2 | 1E-04 | cm/cm/°C |
Melting Temperature | | ISO11357-3 | 224 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC60093 | -- | ohms |
Volume Resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
Comparative Tracking Index | | IEC60112 | 550 | V |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 80 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 100 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
FMVSS Flammability | | FMVSS302 | B | |
Burning Rate | 1.00mm | ISO3795 | <100 | mm/min |
Flammability level | 1.5mm | IEC60695-11-10,-20 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.