PA6 Akulon® F130-C DSM HOLAND
71
- Unit Price:
- $3597 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 44MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Medium viscosity
- Application Areas:film
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Viscosity number | ISO 307 | 196 | cm³/g |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Coefficient of Friction | Dynamic | ISO 8295 | 1.0 | |
| Static | ISO 8295 | 1.2 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Specific Heat Capacity | 1550 | J/kg/°C | ||
| Coefficient of Linear Thermal Expansion (Flow) | ISO 11359-2 | 9.0E-5 | cm/cm/°C |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water Vapor Transmission Rate | 23°C, 85% RH | DIS 15106-1/-3 | 35 | g/m²/24 hr |
| Oxygen Transmission Rate | 0% RH : 23°C | ASTM D256A | 26 | cm³/m²/bar/24 hr |
| 85% RH : 23°C | ASTM D256A | 38 | cm³/m²/bar/24 hr | |
| Film Thickness (Tested) | 50 | µm | ||
| Tensile Modulus | 内部方法 | 455 | Mpa | |
| Tensile Stress (TD) | Yield | ISO 527-3 | 31.0 | Mpa |
| Break | ISO 527-3 | 82.0 | Mpa | |
| Tensile Elongation (MD) | Break | ISO 527-3 | 350 | % |
| Trouser Tear - Parallel | ISO 6383-1 | 32.0 |
| Fill Analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Average Specific Heat Capacity | 20 to 150°C | 2250 | J/kg/°C | |
| Puncture Resistance | 内部方法 | 13.0 | J/cm | |
| RSV - Formic Acid, 1g/100ml | 内部方法 | 3.03 | ||
| Melt Viscosity | 260°C | 内部方法 | 810000 | mPa·s |
| Extrusion | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Take-Off Roll | 110 | °C | ||
| Cylinder Zone 1 Temp | 270 | °C | ||
| Cylinder Zone 2 Temp | 270 | °C | ||
| Die Temperature | 270 | °C | ||
| Cylinder Zone 3 Temp | 270 | °C | ||
| Cylinder Zone 4 Temp | 270 | °C |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Clarity | 内部方法 | 83 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.