Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 275°C/0.325kg | ISO1133 | 9.0 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | | ISO527-2/1 | 2800 | Mpa |
Tensile Stress | Yield | ISO527-2/50 | 65.0 | Mpa |
Tensile Strain | Yield | ISO527-2/50 | 12 | % |
Flexural Modulus | | ISO178 | 2000 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melting temperature | | ISO11357-3 | 218to222 | °C |
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 170 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 75.0 | °C |
Vicat Softening Temperature | | ISO306/B50 | 205 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC60093 | 1E+13 | ohms |
Volume Resistivity | | IEC60093 | 1E+15 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 45 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Scale | ISO2039-2 | 120 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 0.8mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.