Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | (23°C,24hr) | ISO62 | 0.10 | % |
| Moisture Absorption | (23°C,50RH) | ISO62 | 2.50 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Elongation?(Break) | 23°C | ISO527-2 | 4.0 | % |
| Tensile Modulus | 23°C | ISO527-2 | 3700 | Mpa |
| Tensile Strength | 23°C | ISO527-2 | 80 | Mpa |
| Flexural Modulus | 23°C | ISO178 | 3000 | Mpa |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 3.0 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 3.0 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | N/D | kJ/m² |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | Melting Temperature | ISO11357-3 | 220 | °C |
| Deflection Temperature Under Load? | 1.80MPaAnnealed | ISO75-2/Af | 65 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Constant | 23°C | IEC60250 | 3.40 | 1MHz |
| Dissipation Factor? | 23°C | IEC60250 | 0.015 | 1MHz |
| Dissipation Factor? | 相对漏电起痕指数 | IEC60112 | 600 | V |
| Insulation strength | 1.50mm | IEC60243-1 | 13 | KV/mm |
| Volume Resistivity | | IEC60093 | 1E+10 | Ω.cm |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball Indentation Hardness | | ISO2039-1 | 160 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.