Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD:23°C,72小时 | ISO2577 | 0.80to1.0 | % |
Modeling Shrinkage | MD:23°C,72小时 | ISO2577 | 0.30to0.50 | % |
Melt Volume flow Rate | 275°C/5.0kg | ISO1133 | 45.0 | cm3/10min |
Viscosity number | | ISO307 | 145 | cm³/g |
Density | | ISO1183 | 1.36 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Stress | | ISO178 | 270 | Mpa |
Tensile Stress | 断裂 | ISO527-2/5 | 180 | Mpa |
Tensile Strain | 断裂 | ISO527-2/5 | 3.5 | % |
Tensile Modulus | | ISO527-2/1 | 9500 | Mpa |
Flexural Modulus | | ISO178 | 8500 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,未退火 | ISO75-2/B | 220 | °C |
Deflection Temperature Under Load? | 1.8MPa,未退火 | ISO75-2/A | 200 | °C |
Vicat Softening Temperature | | ISO306/B50 | 215 | °C |
Melting temperature | | ISO11357-3 | 222 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC60093 | 1E+13 | ohms |
Volume Resistivity | | IEC60093 | 1E+15 | ohms·cm |
Comparative Tracking Index | 解决方案A | IEC60112 | 500 | V |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 90 | kJ/m² |
Notched Izod impact strength | 23°C | ISO180/1U | 80 | kJ/m² |
Charpy Notched Impact Strength | 23°C | ISO179/1eA | 15 | kJ/m² |
Notched Izod Impact Strength | 23°C | ISO180/1A | 15 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Glow Wire Flammability Index | 1.0到3.0mm | IEC60695-2-12 | 650 | °C |
Burning Rate | | FMVSS302 | <100 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.