Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD:23°C,72小时	ISO2577	1.0to1.2	%
	Modeling Shrinkage	TD:23°C,72小时	ISO2577	1.0to1.2	%
		Modeling Shrinkage	MD:23°C,72小时	ISO2577	0.90to1.1	%
		Modeling Shrinkage	Modeling Shrinkage	MD:23°C,72小时	ISO2577	0.90to1.1	%
Melt Volume flow Rate	275°C/5.0kg	ISO1133	165	cm3/10min
Melt Volume flow Rate	Melt Volume flow Rate	275°C/5.0kg	ISO1133	165	cm3/10min
Viscosity number		ISO307	145	cm³/g
Density		ISO1183	1.14	g/cm³
Density	Density		ISO1183	1.14	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress		ISO178	135	Mpa
Flexural Stress	Flexural Stress		ISO178	135	Mpa
Tensile Modulus		ISO527-2/1	3200	Mpa
Tensile Modulus	Tensile Modulus		ISO527-2/1	3200	Mpa
Flexural Modulus		ISO178	2800	Mpa
	Flexural Modulus		ISO178	2800	Mpa
	Flexural Modulus	Flexural Modulus		ISO178	2800	Mpa
Tensile Stress	屈服	ISO527-2/5	--	Mpa
	Tensile Stress	屈服	ISO527-2/5	--	Mpa
	Tensile Stress	Tensile Stress	屈服	ISO527-2/50	80.0	Mpa
Tensile Strain	断裂	ISO527-2/50	40	%
	Tensile Strain	断裂	ISO527-2/50	40	%
		Tensile Strain	断裂	ISO527-2/5	--	%
			Tensile Strain	断裂	ISO527-2/5	--	%
				Tensile Strain	断裂	ISO527-2/5	--	%
					Tensile Strain	断裂	ISO527-2/5	--	%
						Tensile Strain	断裂	ISO527-2/5	--	%
						Tensile Strain	Tensile Strain	断裂	ISO527-2/50	40	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Melting temperature		ISO11357-3	222	°C
	Melting temperature		ISO11357-3	222	°C
		Melting temperature		ISO11357-3	222	°C
			Melting temperature		ISO11357-3	222	°C
				Melting temperature		ISO11357-3	222	°C
					Melting temperature		ISO11357-3	222	°C
					Melting temperature	Melting temperature		ISO11357-3	222	°C
Deflection Temperature Under Load?	1.8MPa,未退火	ISO75-2/A	65.0	°C
	Deflection Temperature Under Load?	1.8MPa,未退火	ISO75-2/A	65.0	°C
	Deflection Temperature Under Load?	Deflection Temperature Under Load?	0.45MPa,未退火	ISO75-2/B	175	°C
Vicat Softening Temperature		ISO306/B50	200	°C
Vicat Softening Temperature	Vicat Softening Temperature		ISO306/B50	200	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index	解决方案A	IEC60112	600	V
Surface Resistivity		IEC60093	1E+13	ohms
Volume Resistivity		IEC60093	1E+15	ohms·cm
Volume Resistivity	Volume Resistivity		IEC60093	1E+15	ohms·cm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	23°C	ISO179/1eA	5.0	kJ/m²
Notched Izod Impact Strength	23°C	ISO180/1A	5.0	kJ/m²

Flammability	Test Condition	Test Method	Test Result	Unit
Glow Wire Flammability Index	1.0到3.0mm	IEC60695-2-12	750to850	°C
	Glow Wire Flammability Index	1.0到3.0mm	IEC60695-2-12	750to850	°C
	Glow Wire Flammability Index	Glow Wire Flammability Index	1.0到3.0mm	IEC60695-2-12	750to850	°C
Burning Rate		FMVSS302	<100	mm/min
Burning Rate	Burning Rate		FMVSS302	<100	mm/min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.