Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.46 | |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD2.0mm | ISO294-4 | 0.50 | % |
Modeling Shrinkage | TD2.0mm | ISO294-4 | 0.70 | % |
Moisture Absorption | (23°C,24hr,2.00mm) | ISO62 | 5.60 | % |
Moisture Absorption | (23°C,50RH,2.00mm) | ISO62 | 1.60 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Elongation?(Break) | 23°C | ISO527-2 | 3 | % |
Tensile Modulus | 23°C | ISO527-2 | 8300 | Mpa |
Tensile Modulus | | ASTM D638/ISO 527 | 8300 | kg/cm²(MPa)[Lb/in²] |
Tensile Strength | 23°C | ISO527-2 | 140 | Mpa |
Charpy Notched Impact Strength | 23°C | ISO179/1eA | 7 | kJ/m² |
Charpy Notched Impact Strength | -30°C | ISO179/1eA | 5.50 | kJ/m² |
Notched Izod Impact Strength | 23°C | ISO180/1A | 5.50 | kJ/m² |
Notched Izod Impact Strength | -30°C | ISO180/1A | 4.00 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 60 | kJ/m² |
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 50 | kJ/m² |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Coefficient of Linear Thermal Expansion | MD | ISO11359-2 | 4.1E-05 | cm/cm/°C |
Coefficient of Linear Thermal Expansion | TD | ISO11359-2 | 7.7E-05 | cm/cm/°C |
Vicat Softening Temperature | | ISO306/B50 | 210 | °C |
Vicat Softening Temperature | 玻璃转化温度 | ISO11357-2 | 70 | °C |
Vicat Softening Temperature | Melting Temperature | ISO11357-3 | 221 | °C |
Deflection Temperature Under Load? | 0.45MPaUnannealed | ISO75-2/Bf | 215 | °C |
Deflection Temperature Under Load? | 1.80MPaAnnealed | ISO75-2/Af | 195 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dissipation Factor? | 23°C | IEC60250 | 0.013 | 100HZ |
Dissipation Factor? | 23°C | IEC60250 | 3.8E-03 | 1MHz |
Dissipation Factor? | 相对漏电起痕指数 | IEC60112 | 500 | V |
Insulation strength | | IEC60243-1 | 33 | KV/mm |
Volume Resistivity | | IEC60093 | >1.0E+15 | Ω.cm |
Processing | Test Condition | Test Method | Test Result | Unit |
---|
Mold Temperature | | | 70-120 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.