PA6 Ultramid® 8231G HS BASF GERMANY

Unit Price:
$3753 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	24hr	ASTMD570	0.90	%
	Moisture Absorption	饱和	ASTMD570	4.0	%
	Moisture Absorption	Moisture Absorption	平衡,50%RH	ASTMD570	1.1	%
Density		ASTMD792	1.62	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Strength	断裂,23°C	ASTMD638	157	Mpa
Tensile Elongation	断裂,23°C	ASTMD638	3.0	%
Flexural Modulus	23°C	ASTMD790	8970	Mpa
Flexural Strength	23°C	ASTMD790	232	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	1.8MPa,未退火	ASTMD648	195	°C
RTI Str	0.8mm	UL746	105	°C
	RTI Str	1.5mm	UL746	115	°C
		RTI Str	2.5mm	UL746	115	°C
		RTI Str	RTI Str	3.0mm	UL746	120	°C
RTI Imp	0.8mm	UL746	105	°C
	RTI Imp	1.5mm	UL746	115	°C
		RTI Imp	2.5mm	UL746	115	°C
		RTI Imp	RTI Imp	3.0mm	UL746	115	°C
RTI Elec	0.8mm	UL746	130	°C
	RTI Elec	1.5mm	UL746	130	°C
		RTI Elec	2.5mm	UL746	130	°C
		RTI Elec	RTI Elec	3.0mm	UL746	130	°C
Peak Melting Temperature		ASTMD3418	220	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume Resistivity	1.50mm	ASTMD257	>1.0E+13	ohms·cm
Dielectric Strength	1.50mm	ASTMD149	29	KV/mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Notched Izod Impact Strength	23°C	ASTMD256	110	J/m

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.