PA6 Ultramid® B3WG6 BK BASF GERMANY
185
- Unit Price:
- $2951 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Oil resistant Filler: Glass fiber reinf 30% filler by weight
- Application Areas:Engine hood parts Automotive sector Application in the automo
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.18mm | 0.30 | % | |
| Water absorption rate | Saturation | ASTMD570 | 6.6 | % |
| Saturation,23°C | ISO62 | 6.6 | % | |
| Equilibrium,50%RH | ASTMD570 | 2.1 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 2.1 | % | |
| Melt volume flow rate | 275°C/5.0kg | ISO1133 | 40.0 | cm3/10min |
| Density/specific gravity | ASTMD792 | 1.36 | g/cm³ | |
| ISO1183 | 1.36 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ISO527-2 | 9500 | Mpa |
| Bending modulus | 23°C | ISO178 | 8300 | Mpa |
| Tensile stress | Break,23°C | ISO527-2 | 180 | Mpa |
| Tensile strain | Break,23°C | ISO527-2 | 3.0 | % |
| Tensile strength | Break,23°C | ASTMD638 | 180 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Peak melting temperature | ASTMD3418 | 220 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ASTMD648 | 220 | °C |
| 0.45MPa,Unannealed | ISO75-2/B | 220 | °C | |
| 1.8MPa,Unannealed | ASTMD648 | 210 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 205 | °C | |
| Melting temperature (DSC) | ISO3146 | 220 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179 | 9.0 | kJ/m² |
| 23°C | ISO179 | 12 | kJ/m² | |
| Impact strength of cantilever beam gap | -40°C | ASTMD256 | 110 | J/m |
| 23°C | ASTMD256 | 150 | J/m | |
| 23°C | ISO180 | 12 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO179 | 65 | kJ/m² |
| 23°C | ISO179 | 80 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.