PA6 Ultramid® 6030G HS BK BASF GERMANY
121
- Unit Price:
- $3258 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 50MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Oil resistant High impact resistance
- Application Areas:film Electrical enclosure
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.36 |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO62 | 1.1 | % |
| Saturation,23°C | ISO62 | 6.7 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 1.9 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Break,-40°C | ISO527-2 | 220 | Mpa |
| Break,23°C | ISO527-2 | 155 | Mpa | |
| Break,80°C | ISO527-2 | 80.0 | Mpa | |
| Break,120°C | ISO527-2 | 65.0 | Mpa | |
| Break,150°C | ISO527-2 | 60.0 | Mpa | |
| Tensile strain | Break,23°C | ISO527-2 | 3.0 | % |
| Tensile modulus | 120°C | ISO527-2 | 2730 | Mpa |
| 150°C | ISO527-2 | 2890 | Mpa | |
| -40°C | ISO527-2 | 8740 | Mpa | |
| 23°C | ISO527-2 | 9580 | Mpa | |
| 80°C | ISO527-2 | 3820 | Mpa | |
| Rockwell hardness | ASTM D785 | 121 | ||
| Bending modulus | 23°C | ISO178 | 8070 | Mpa |
| Bending stress | 23°C | ISO178 | 230 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTIElec | 0.8mm | UL746 | 130 | °C |
| 1.5mm | UL746 | 140 | °C | |
| 3.0mm | UL746 | 140 | °C | |
| Evolution Calendar intelligent importer | 0.8mm | UL746 | 115 | °C |
| 1.5mm | UL746 | 115 | °C | |
| 3.0mm | UL746 | 120 | °C | |
| RTIStr | 0.8mm | UL746 | 130 | °C |
| 1.5mm | UL746 | 140 | °C | |
| 3.0mm | UL746 | 140 | °C | |
| Linear coefficient of thermal expansion | MD | 2.5E-05 | cm/cm/°C | |
| TD | 6.7E-05 | cm/cm/°C | ||
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 219 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 205 | °C | |
| Melting temperature (DSC) | ISO3146 | 220 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC60093 | >1.0E+13 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 54 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| 3.0mm | UL94 | HB | ||
| 0.8mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.