PA6 Ultramid® 8253HS BK102 BASF GERMANY
94
- Unit Price:
- $4458 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 37MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability high strength Oil resistant
- Application Areas:Helmet Gear Automotive Applications
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.18mm | 1.2 | % | |
| Moisture Absorption | 24hr | ASTMD570 | 1.5 | % |
| 23°C,24hr | ISO62 | 1.5 | % | |
| Saturation | ASTMD570 | 8.1 | % | |
| Saturation,23°C | ISO62 | 8.1 | % | |
| Equilibrium,50%RH | ASTMD570 | 2.3 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 2.3 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | 23°C | ISO527-2 | 2400 | Mpa |
| Tensile Elongation | Break,23°C | ASTMD638 | >100 | % |
| Yield,23°C | ASTMD638 | 4.0 | % | |
| Flexural Modulus | 23°C | ASTMD790 | 2270 | Mpa |
| 23°C | ISO178 | 1900 | Mpa | |
| Flexural Strength | 23°C | ASTMD790 | 85.0 | Mpa |
| Tensile Stress | Yield,23°C | ISO527-2 | 60.0 | Mpa |
| Tensile Strain | Yield,23°C | ISO527-2 | 4.0 | % |
| Flexural Stress | 23°C | ISO178 | 65.0 | Mpa |
| Nominal Tensile Strain at Break | 23°C | ISO527-2 | 40 | % |
| Tensile Strength | Yield,23°C | ASTMD638 | 65.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Peak Melting Temperature | ASTMD3418 | 220 | °C | |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 160 | °C |
| 1.8MPa,Unannealed | ASTMD648 | 60.0 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 55.0 | °C | |
| Melting temperature (DSC) | ISO3146 | 220 | °C | |
| RTIElec | 0.71mm | UL746 | 105 | °C |
| 0.75mm | UL746 | 105 | °C | |
| 1.5mm | UL746 | 105 | °C | |
| 3.0mm | UL746 | 105 | °C | |
| 6.0mm | UL746 | 105 | °C | |
| Evolution Calendar intelligent importer | 0.71mm | UL746 | 95.0 | °C |
| 0.75mm | UL746 | 95.0 | °C | |
| 1.5mm | UL746 | 105 | °C | |
| 3.0mm | UL746 | 105 | °C | |
| 6.0mm | UL746 | 105 | °C | |
| RTIStr | 0.71mm | UL746 | 95.0 | °C |
| 0.75mm | UL746 | 95.0 | °C | |
| 1.5mm | UL746 | 105 | °C | |
| 3.0mm | UL746 | 105 | °C | |
| 6.0mm | UL746 | 105 | °C | |
| Linear thermal expansion coefficient | MD | ASTME831 | 9.9E-05 | cm/cm/°C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179 | NoBreak | |
| Drop Impact Resistance | 23°C | 内部方法 | 271 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R-Scale | ASTMD785 | 82 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 3.0mm | UL94 | HB | ||
| 6.0mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.