Material Description

Technical Data Sheet

Material Description

Material Properties:Thermal stability high strength Oil resistant
Application Areas:Helmet Gear Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD：3.18mm		0.90	%
Moisture Absorption	24hr	ASTMD570	1.6	%
	Moisture Absorption	23°C,24hr	ISO62	1.6	%
		Moisture Absorption	Saturation	ASTMD570	9.3	%
			Moisture Absorption	Saturation,23°C	ISO62	9.3	%
				Moisture Absorption	Equilibrium,50%RH	ASTMD570	2.6	%
				Moisture Absorption	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	2.6	%
Density / Specific Gravity		ISO1183	1.13	g/cm³
Density / Specific Gravity	Density / Specific Gravity		ASTMD792	1.13	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Stress	Yield,120°C	ISO527-2	30.0	Mpa
	Tensile Stress	Yield,150°C	ISO527-2	25.0	Mpa
		Tensile Stress	Yield,-40°C	ISO527-2	137	Mpa
			Tensile Stress	Yield,23°C	ISO527-2	88.0	Mpa
			Tensile Stress	Tensile Stress	Yield,80°C	ISO527-2	40.0	Mpa
Tensile Strain	Yield,23°C	ISO527-2	4.0	%
Flexural Stress	23°C	ISO178	95.0	Mpa
Nominal Tensile Strain at Break	-40°C	ISO527-2	5.0	%
	Nominal Tensile Strain at Break	23°C	ISO527-2	7.0	%
		Nominal Tensile Strain at Break	80°C	ISO527-2	>100	%
		Nominal Tensile Strain at Break	Nominal Tensile Strain at Break	120°C	ISO527-2	>100	%
Tensile Strength	Yield,-40°C	ASTMD638	137	Mpa
	Tensile Strength	Yield,23°C	ASTMD638	90.0	Mpa
		Tensile Strength	Yield,80°C	ASTMD638	40.0	Mpa
			Tensile Strength	Yield,121°C	ASTMD638	30.0	Mpa
				Tensile Strength	Break,-40°C	ASTMD638	130	Mpa
					Tensile Strength	Break,23°C	ASTMD638	90.0	Mpa
						Tensile Strength	Break,80°C	ASTMD638	35.0	Mpa
						Tensile Strength	Tensile Strength	Break,121°C	ASTMD638	25.0	Mpa
Tensile Modulus	80°C	ISO527-2	750	Mpa
	Tensile Modulus	120°C	ISO527-2	550	Mpa
		Tensile Modulus	150°C	ISO527-2	445	Mpa
			Tensile Modulus	-40°C	ISO527-2	4090	Mpa
			Tensile Modulus	Tensile Modulus	23°C	ISO527-2	3700	Mpa
Tensile Elongation	Yield,-40°C	ASTMD638	3.0	%
	Tensile Elongation	Yield,23°C	ASTMD638	4.0	%
		Tensile Elongation	Yield,80°C	ASTMD638	25	%
			Tensile Elongation	Yield,121°C	ASTMD638	27	%
				Tensile Elongation	Break,-40°C	ASTMD638	5.0	%
					Tensile Elongation	Break,23°C	ASTMD638	12	%
						Tensile Elongation	Break,80°C	ASTMD638	>100	%
						Tensile Elongation	Tensile Elongation	Break,121°C	ASTMD638	>100	%
Flexural Modulus	23°C	ASTMD790	3170	Mpa
	Flexural Modulus	65°C	ASTMD790	600	Mpa
		Flexural Modulus	90°C	ASTMD790	440	Mpa
			Flexural Modulus	121°C	ASTMD790	385	Mpa
				Flexural Modulus	23°C	ISO178	2800	Mpa
				Flexural Modulus	Flexural Modulus	-40°C	ASTMD790	3370	Mpa
Flexural Strength	-40°C	ASTMD790	183	Mpa
	Flexural Strength	23°C	ASTMD790	110	Mpa
		Flexural Strength	65°C	ASTMD790	30.0	Mpa
		Flexural Strength	Flexural Strength	121°C	ASTMD790	21.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed	ASTMD648	190	°C
	Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	165	°C
		Deflection Temperature Under Load?	1.8MPa,Unannealed	ASTMD648	75.0	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	65.0	°C
Melting temperature (DSC)		ISO3146	220	°C
RTIElec	0.71mm	UL746	130	°C
	RTIElec	1.5mm	UL746	130	°C
		RTIElec	3.0mm	UL746	130	°C
		RTIElec	RTIElec	6.0mm	UL746	130	°C
Evolution Calendar intelligent importer	0.71mm	UL746	95.0	°C
	Evolution Calendar intelligent importer	1.5mm	UL746	105	°C
		Evolution Calendar intelligent importer	3.0mm	UL746	105	°C
		Evolution Calendar intelligent importer	Evolution Calendar intelligent importer	6.0mm	UL746	105	°C
RTIStr	0.71mm	UL746	95.0	°C
	RTIStr	1.5mm	UL746	105	°C
		RTIStr	3.0mm	UL746	105	°C
		RTIStr	RTIStr	6.0mm	UL746	105	°C
Linear thermal expansion coefficient	MD	ASTME831	8.1E-05	cm/cm/°C
Peak Melting Temperature		ASTMD3418	220	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index		IEC60112	600	V
Volume Resistivity	1.50mm	ASTMD257	>1.0E+13	ohms·cm
Dielectric Strength	1.50mm	ASTMD149	30	KV/mm
Volume Resistivity		IEC60093	>1.0E+13	ohms·cm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Drop Impact Resistance	23°C	内部方法	122	J
Charpy Unnotched Impact Strength	23°C	ISO179	NoBreak
Charpy Notched Impact Strength	23°C	ISO179	3.5	kJ/m²
Notched Izod Impact Strength	-40°C	ASTMD256	32	J/m
Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ASTMD256	48	J/m

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Scale	ASTMD785	120

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5mm	UL94	V-2
	UL flame retardant rating	3.0mm	UL94	V-2
		UL flame retardant rating	6.0mm	UL94	V-2
		UL flame retardant rating	UL flame retardant rating	0.71mm	UL94	V-2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.