PA6 Ultramid® B3WG3 BASF GERMANY
93
- Unit Price:
- $3620 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 15MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Oil resistant
- Application Areas:Engine parts Shell
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ASTM D792/ISO 1183 | 1230 | ||
| Modeling Shrinkage | ASTM D955 | 0.45 | % | |
| Moisture Absorption 23℃/24H | ASTM D570/ISO 62 | 8 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | 3.5 | % | |
| Tensile Modulus | ASTM D638/ISO 527 | 5800 | kg/cm²(MPa)[Lb/in²] | |
| 23°C | ISO527-2 | 5800 | Mpa | |
| 干燥 | MPa | ISO 527-2 | ||
| Tensile Strength | ASTM D638/ISO 527 | 130(断裂) | kg/cm²(MPa)[Lb/in²] | |
| Flexural Modulus | ASTM D790/ISO 178 | 5300 | kg/cm²(MPa)[Lb/in²] | |
| 23°C | ISO178 | 5400 | Mpa | |
| Flexural Strength | 干燥 | MPa | IS 178 | 180 |
| ASTM D790/ISO 178 | 200 | kg/cm²(MPa)[Lb/in²] | ||
| Tensile Stress(Yield) | 干燥 | MPa | ISO 527-2 | 130 |
| Charpy Notched Impact Strength | 23℃ | KJ/m | ISO 179/1eA | |
| Tensile Elongation (Yield) | 干燥 | % | ISO 527-2 | |
| Tensile Stress | Break,23°C | ISO527-2 | 130 | Mpa |
| Tensile Strain | Break,23°C | ISO527-2 | 3.5 | % |
| Charpy impact strength | 23℃ | KJ/m | ISO 179/1eU | |
| ASTM D256/ISO 179 | 6 | kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 45 | kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 50 | kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 5 | kg·cm/cm(J/M)ft·lb/in |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning Rate | UL94 | HB | ||
| Deflection Temperature Under Load? | ASTM D648/ISO 75 | 198 | ℃（℉） | |
| ASTM D648/ISO 75 | 218 | ℃（℉） | ||
| 1.8MPa,Unannealed | ISO75-2/A | 190 | °C | |
| 1.8Mpa | ℃ | ISO 75-2 | 190 | |
| 0.45Mpa | ℃ | ISO 75-2 | 215 | |
| Flame retardancy | UL94 | HB | ||
| Melting temperature (DSC) | ISO3146 | 220 | °C | |
| RTIElec | 0.8mm | UL746 | 130 | °C |
| 1.5mm | UL746 | 130 | °C | |
| 3.0mm | UL746 | 130 | °C | |
| Evolution Calendar intelligent importer | 1.5mm | UL746 | 85.0 | °C |
| 3.0mm | UL746 | 85.0 | °C | |
| RTIStr | 1.5mm | UL746 | 130 | °C |
| 3.0mm | UL746 | 130 | °C | |
| Melting temperature | ℃ | ISO 3146 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation Factor | 10 | IEC 250 | 250 | |
| Dielectric Constant | IEC 250 | 3.8 | ||
| Volume Resistivity | ASTM D257/IEC 60093 | >1E 13 | Ω.cm | |
| Ω.cm | IEC 93 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179 | 40 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 3.0mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.