PA6 Ultramid® B3EG5 BASF GERMANY
96
- Unit Price:
- $2485 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 136.3MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:enhance
- Application Areas:Automotive sector
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ASTM D792/ISO 1183 | 1320 | ||
| Modeling Shrinkage | ASTM D955 | 0.35 | % | |
| Moisture Absorption 23℃/24H | ASTM D570/ISO 62 | 6.8-7.4 | % | |
| Melt Mass-Flow Rate | ASTM D1238/ISO 1133 | 55 （cm3/10min 275℃/5kg ) | g/10min |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | 23℃ | % | 0,20到1,0 |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | 干/湿 | 8000/5500 | Mpa | |
| Tensile Creep Modulus | 1000h，湿 | 3000 | Mpa | |
| Tensile Stress | Break,23℃ | MPa | 95.17到284.83 | |
| Tensile Strain | Break,23℃ | % | 2,5到3,0 | |
| Ball Indentation Hardness | 干/湿 | 210/140 | Mpa | |
| Tensile Stress (Break) | 干/湿 | 160/105 | Mpa | |
| Notched Izod Impact Strength | 30℃，干/湿 | 10 | KJ/m | |
| +23℃，干/湿 | 12/25 | KJ/m | ||
| Notched Izod Impact Strength | 干/湿 | 80/105 | KJ/m | |
| 30℃，干 | 75 | KJ/m | ||
| Tensile Elongation (Yield, 50mm/min) | 干/湿 | 3.5/8.5 | % | |
| Tensile Modulus | ASTM D638/ISO 527 | 8000 | kg/cm²(MPa)[Lb/in²] | |
| 23℃ | MPa | 0.01,0.01E0.05到0.01,0.04E0.05 | ||
| Tensile Elongation | ≤0.5%, +23℃，湿 | 3000 | Mpa | |
| Flexural Modulus | 干/湿 | 7400/4200 | Mpa | |
| ASTM D790/ISO 178 | 7400 | kg/cm²(MPa)[Lb/in²] | ||
| Flexural Strength | ASTM D790/ISO 178 | 2020 | kg/cm²(MPa)[Lb/in²] | |
| 干/湿 | 220/150 | Mpa | ||
| Tensile Stress (Yield 50mm/min) | 干/湿 | 160/105 | Mpa | |
| Notched Izod Impact Strength | +23℃，干/湿 | 12/17 | KJ/m | |
| Tensile Elongation (Break, 50mm/min) | 干/湿 | 3.5/8.5 | % | |
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | 3.5 | % | |
| Charpy impact strength | ASTM D256/ISO 179 | 80 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 10 | kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 12 | kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 75 | kg·cm/cm(J/M)ft·lb/in | ||
| Izod notch impact strength | ASTM D256/ISO 179 | 12 | kg·cm/cm(J/M)ft·lb/in |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Coefficient of Linear Thermal Expansion | 23-80℃Dry | 2-2.5/6-7 | ||
| Continuous Use Temperature | 200 | °C | ||
| Temperature Index | 在20000h/5000h，后拉伸强度下降50%时 | 120/150 | °C | |
| Burning Rate | UL94 | HB | ||
| Deflection Temperature Under Load? | ASTM D648/ISO 75 | 210(1.80MPa) | ℃（℉） | |
| 0.45MPa负荷，Dry | 220 | °C | ||
| 1.8MPa,Unannealed | °C | 239到261 | ||
| 1.8MPa负荷，Dry | 210 | °C | ||
| Melting Temperature | 220 | ℃（℉） | ||
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.2-0.25 | mm/mm.℃ | |
| Thermal Conductivity | Dry | 0.26 | W/(m.K) | |
| Specific Heat | Dry | 1.5 | J/(g.K) |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric Constant | ASTM D150/IEC 60250 | 3.8 | ||
| 1MHz，干/湿 | 3.8/7 | |||
| Volume Resistivity | ASTM D257/IEC 60093 | 1E 13 | Ω.cm | |
| Surface resistance | 干/湿 | 10 | Ω | |
| Taber Abrasion Resistance | 1MHz，干/湿 | 0.025/0.24 | ||
| Dielectric Strength | K20/P50，干/湿 | 80/70 | KV/mm | |
| Volume Resistivity | 干/湿 | 10 | Ω.cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | 23℃ | kJ/m² | 10.679到17.642 |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Notched Izod Impact Strength | +23℃干/湿 | 10/30 | J | |
| Comparative Tracking Index | 干/湿 | 干/湿 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.