PA6 Amilan® CM1056 TORAY JAPAN
105
- Unit Price:
- $2839 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Blow molding grade
Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.09 | ||
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 1.7 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 23°C,24hr | % | 1.7 | -- |
| Saturation,23°C | % | 8.0 | -- |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | ASTM D785 | 114 | ||
| Tensile stress | -40°C | MPa | 105 | 95.0 |
| 23°C | MPa | 60.0 | 35.0 | |
| bending strength | 23℃ | ASTM D-790 | Dry｜80 | Mpa |
| 23℃ | ASTM D-790 | 3.0%Water｜- | Mpa | |
| Tensile yield strength | -40℃ | ASTM D-638 | Dry｜105 | Mpa |
| -40℃ | ASTM D-638 | 3.0%Water｜95 | Mpa | |
| Rockwell hardness | 23℃ | ASTM D-785 | Dry｜114 | R scale |
| Bending modulus | -40℃ | ASTM D-790 | 3.0%Water｜- | GPa |
| 23℃ | ASTM D-790 | Dry｜2.1 | GPa | |
| 23℃ | ASTM D-790 | 3.0%Water｜0.7 | GPa | |
| 80℃ | ASTM D-790 | Dry｜0.5 | GPa | |
| 80℃ | ASTM D-790 | 3.0%Water｜- | GPa | |
| IZOD notch free impact strength | 23℃ | ASTM D-256 | Dry｜不断裂 | kJ/m² |
| 23℃ | ASTM D-256 | 3.0%Water｜- | kJ/m² | |
| elongation at break | -40℃ | ASTM D-638 | Dry｜15 | % |
| -40℃ | ASTM D-638 | 3.0%Water｜5.0 | % | |
| Tensile yield strength | 80℃ | ASTM D-638 | Dry｜25 | Mpa |
| Rockwell hardness | 23℃ | ASTM D-785 | 3.0%Water｜- | R scale |
| IZOD notch impact strength | 23℃ | ASTM D-256 | Dry｜205 | J/m |
| 23℃ | ASTM D-256 | 3.0%Water｜690 | J/m | |
| -40℃ | ASTM D-256 | Dry｜175 | J/m | |
| -40℃ | ASTM D-256 | 3.0%Water｜- | J/m | |
| elongation at break | 23℃ | ASTM D-638 | Dry｜<200 | % |
| 23℃ | ASTM D-638 | 3.0%Water｜<200 | % | |
| 80℃ | ASTM D-638 | Dry｜<200 | % | |
| 80℃ | ASTM D-638 | 3.0%Water｜<200 | % | |
| Bending modulus | -40℃ | ASTM D-790 | Dry｜2.9 | GPa |
| Tensile yield strength | 80℃ | ASTM D-638 | 3.0%Water｜20 | Mpa |
| 23℃ | ASTM D-638 | Dry｜60 | Mpa | |
| 23℃ | ASTM D-638 | 3.0%Water｜35 | Mpa | |
| bending strength | -40℃ | ASTM D-790 | Dry｜130 | Mpa |
| -40℃ | ASTM D-790 | 3.0%Water｜- | Mpa | |
| Tensile stress | 80°C | MPa | 25.0 | 20.0 |
| Tensile strain | Break,-40°C | % | 3.5 | 1.0 |
| Break,23°C | % | 50 | ||
| Break,80°C | % | 50 | ||
| Bending modulus | -40°C | MPa | 2900 | -- |
| 23°C | MPa | 2100 | 700 | |
| 80°C | MPa | 500 | -- | |
| Bending stress | -40°C | MPa | 130 | -- |
| 23°C | MPa | 80.0 | -- | |
| Taber abraser | 1000Cycles | mg | 6.00到7.00 | -- |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.86MPa | ASTM D-648 | 3.0%Water｜- | °C |
| 0.46MPa | ASTM D-648 | Dry｜160 | °C | |
| 0.46MPa | ASTM D-648 | 3.0%Water｜- | °C | |
| Linear expansion coefficient | ASTM D-696 | Dry｜8-9 | 10-5/℃ | |
| ASTM D-696 | 3.0%Water｜- | 10-5/℃ | ||
| melting point | DSC | Dry｜225 | °C | |
| DSC | 3.0%Water｜- | °C | ||
| Hot deformation temperature | 1.86MPa | ASTM D-648 | Dry｜67 | °C |
| 0.45MPa,Unannealed | °C | 160 | -- | |
| 1.8MPa,Unannealed | °C | 51.0 | -- | |
| Melting temperature | °C | 225 | -- | |
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 8.0E-5到9.0E-5 | -- |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C | kJ/m² | 16 | 54 |
| 23°C | 无断裂 | -- |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Sale,23°C | 114 | -- |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 23℃ | ASTM D-570 | Dry｜8.0 | % |
| 23℃ | ASTM D-570 | 3.0%Water｜- | % | |
| 23℃，24hr | ASTM D-570 | Dry｜1.7 | % | |
| 23℃，24hr | ASTM D-570 | 3.0%Water｜- | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.