Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D792/ISO 1183 | 1.29 | |
| Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 1.3 | % |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD:3.00mm3 | % | 0.60到0.90 | -- |
| Modeling Shrinkage | MD:3.00mm4 | % | 0.30到0.50 | -- |
| Moisture Absorption | 23°C,24hr | % | 1.3 | -- |
| Moisture Absorption | Saturation,23°C | % | 7.8 | -- |
| Reinforcement Content | | | 20 | wt% |
| Taber wear | (1000g,CS-17)23 ℃ | ASTM D-1044 | 12 | mg/1000次 |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Taber Abrasion Resistance | 1000Cycles | mg | 0.300 | -- |
| Compressive Stress | 23°C | MPa | 155 | 80.0 |
| Compressive Stress | 80°C | MPa | 90.0 | -- |
| Compressive Stress | -40°C | MPa | 240 | -- |
| Shearing Strength | 23°C | MPa | 115 | 65.0 |
| Coefficient of Friction (vs.Metal) | | | 0.15 | -- |
| Tensile Strength (Yield) | 23℃ | ASTM D-638 | 1200 | kg/cm |
| Tensile Elongation (Break) | 23℃ | ASTM D-638 | 5 | % |
| Notched Izod Impact Strength | 23℃ V-Notched1/2 | ASTM D-256 | 6 | kg·cm/cm |
| Tensile Stress | 23°C | MPa | 120 | -- |
| Tensile Strain | Break,-40°C | % | 2.5 | 3.0 |
| Tensile Strain | Break,23°C | % | 3.0 | |
| Tensile Strain | Break,80°C | % | 5.0 | 5.5 |
| Rockwell Hardness | | ASTM D785 | R120,M92 | |
| Rockwell Hardness | R-标度 23℃ | ASTM D-785 | 120 | |
| Rockwell Hardness | M-标度 23℃ | ASTM D-785 | 92 | |
| Flexural Modulus | -40°C | MPa | 8700 | 7300 |
| Flexural Modulus | 23°C | MPa | 6800 | 3500 |
| Flexural Modulus | 80°C | MPa | 3200 | 2600 |
| Flexural Stress | -40°C | MPa | 275 | -- |
| Flexural Stress | 23°C | MPa | 205 | -- |
| Flexural Stress | 80°C | MPa | 115 | -- |
| Flexural strength | 23℃ | ASTM D-790 | 1800 | kg/cm |
| Flexural strength | 80℃ | ASTM D-790 | 1000 | kg/cm |
| Flexural strength | -40℃ | ASTM D-790 | 2400 | kg/cm |
| Flexural Modulus | -40℃ | ASTM D-790 | 78000 | kg/cm |
| Flexural Modulus | 23℃ | ASTM D-790 | 60000 | kg/cm |
| Flexural Modulus | 80℃ | ASTM D-790 | 29000 | kg/cm |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Specific Heat | | | 0.36 | Cal/g·℃ |
| Specific Heat | | J/kg/°C | 1600 | -- |
| Thermal Conductivity | | W/m/K | 0.33 | -- |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | °C | 215 | -- |
| Melting Temperature | | 差示扫描测热计DSC | 225 | °C |
| Melting Temperature | | | 225 | ℃（℉） |
| Deflection Temperature Under Load | 18.6kg/cm | ASTM D-648 | 185 | °C |
| Deflection Temperature Under Load | 4.6kg/cm | ASTM D-648 | 215 | °C |
| Linear thermal expansion coefficient | MD | cm/cm/°C | 3E-05 | -- |
| Melting temperature | | °C | 225 | -- |
| Coefficient of Linear Thermal Expansion | | ASTM D-696 | 3 | |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Strength | | kV/mm | 20 | -- |
| Dielectric Strength | 1/8" 短时间 | ASTM D-149 | 20 | KV/mm |
| Dissipation Factor | 23°C,1MHz | | 0.030 | -- |
| Dissipation Factor | 23°C,50Hz | | 0.040 | -- |
| Dissipation Factor | 23°C,1kHz | | 0.040 | -- |
| Arc Resistance | | sec | 120 | -- |
| Dielectric Constant | 23°C,50Hz | | 4.60 | -- |
| Dielectric Constant | 23°C,1kHz | | 4.40 | -- |
| Dielectric Constant | 23°C,1MHz | | 3.80 | -- |
| Volume Resistivity | | ASTM D257/IEC 60093 | 10^13 | Ω.cm |
| Volume Resistivity | | ohms·cm | 1E+15 | 1E+12 |
| Volume Resistivity | | ASTM D-257 | 10 | Ω·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -40°C | kJ/m² | 25 | |
| Charpy Unnotched Impact Strength | 23°C | kJ/m² | 55 | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | M-Sale,23°C | | 92 | -- |
| Rockwell Hardness | R-Sale,80°C | | 12 | -- |
| Rockwell Hardness | R-Sale,23°C | | 120 | -- |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.6mm | | HB | -- |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 24hr 23℃ | ASTM D-570 | 1.3 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.