Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D792/ISO 1183 | 1.13 | |
| Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 1.8 | % |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD：1.00mm3 | % | 0.70到1.1 | -- |
| Modeling Shrinkage | MD：3.00mm4 | % | 1.2到1.8 | -- |
| Moisture Absorption | 23°C,24hr | % | 1.8 | -- |
| Moisture Absorption | Saturation,23°C | % | 11 | -- |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | -40°C | MPa | 110 | |
| Tensile Stress | 23°C | MPa | 80.0 | 35.0 |
| Tensile Stress | 80°C | MPa | 25.0 | 20.0 |
| Tensile Strain | Yield,23°C | % | 1.5 | -- |
| Tensile Strain | Break,23°C | % | 38 | |
| Rockwell Hardness | | ASTM D785 | 80 | |
| Flexural Modulus | -40°C | MPa | 3800 | 3600 |
| Flexural Modulus | 23°C | MPa | 2800 | |
| Flexural Modulus | 80°C | MPa | 700 | 300 |
| Flexural Stress | -40°C | MPa | 135 | |
| Flexural Stress | 23°C | MPa | 110 | 40.0 |
| Flexural Stress | 80°C | MPa | 40.0 | 25.0 |
| Taber Abrasion Resistance | 1000Cycles | mg | 3.00到4.00 | -- |
| Compressive Stress | 23°C | MPa | 80.0 | -- |
| Shearing Strength | 23°C | MPa | 70.0 | 65.0 |
| Coefficient of Friction (vs.Metal) | | | 0.15到0.20 | -- |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear thermal expansion coefficient | MD | cm/cm/°C | 8E-05 | -- |
| Melting temperature | | °C | 225 | -- |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | °C | 182 | -- |
| Melting Temperature | | | 225 | ℃（℉） |
| Specific Heat | | J/kg/°C | 1900 | -- |
| Thermal Conductivity | | W/m/K | 0.25 | -- |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume Resistivity | | ASTM D257/IEC 60093 | 10^12~13 | Ω.cm |
| Volume Resistivity | | ohms·cm | 1.0E+14到1.0E+15 | 1.0E+11到1.0E+12 |
| Comparative Tracking Index | CTI | V | 600 | -- |
| Dielectric Strength | | kV/mm | 20 | -- |
| Dissipation Factor | 23°C,50Hz | | 0.070 | 0.10 |
| Dissipation Factor | 23°C,1kHz | | 0.060 | 0.11 |
| Dissipation Factor | 23°C,1MHz | | 0.030 | 0.13 |
| Arc Resistance | | sec | 120 | -- |
| Dielectric Constant | 23°C,50Hz | | 4.10 | 9.00 |
| Dielectric Constant | 23°C,1kHz | | 3.90 | 8.00 |
| Dielectric Constant | 23°C,1MHz | | 3.40 | 4.50 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -40°C | | 无断裂 | -- |
| Charpy Unnotched Impact Strength | 23°C | | 无断裂 | -- |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R-Sale,23°C | | 119 | |
| Rockwell Hardness | R-Sale,80°C | | 80 | -- |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.79mm | | V-2 | -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.