Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 230℃,2.16kg | ISO 1133 | 22 | g/10min |
| Modeling Shrinkage | | Internal Method | 1.4-1.8 | % |
| Modeling Shrinkage | | 内部方法 | 1.4到1.8 | % |
| Melt Mass-Flow Rate | 230°C/2.16kg | ISO1133 | 22 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Elongation (Break) | | ISO 527-2 | 200 | % |
| Tensile Elongation (Break) | 简支梁Notched冲击强度，23℃ | ISO 179 | 6.0 | kJ/m² |
| Tensile Elongation (Break) | 洛氏硬度 | ISO 2039-2 | 76 | |
| Breaking tensile strain | | ISO 527-2 | 17 | % |
| Nominal Tensile Strain at Break | | ISO527-2 | 200 | % |
| Flexural Stress | | ISO178 | 29.0 | Mpa |
| Tensile Stress(Yield) | | ISO 527-2 | 27 | Mpa |
| Tensile Stress | Yield | ISO527-2 | 27.0 | Mpa |
| Tensile Strain | Break | ISO527-2 | 17 | % |
| Tensile Modulus | | ISO527-2 | 950 | Mpa |
| Tensile Modulus | | ISO 527-2 | 950 | Mpa |
| Flexural Modulus | | ISO178 | 950 | Mpa |
| Flexural Modulus | | ISO 178 | 950 | Mpa |
| Flexural Strength | | ISO 178 | 29 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 78.0 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179 | 6.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R-Sale | ISO2039-2 | 76 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Haze | 2000µm | ISO14782 | 30 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.