Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 230℃，2.16kg 230℃/2.16 kg | ISO 1133 | 1.9 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Modulus | | ISO 178 | 750 | Mpa |
| Coefficient of Friction | | ISO 8295 | > 0.70 | |
| Films | Test Condition | Test Method | Test Result | Unit |
|---|
| Film Thickness | 测试 经测试 | | 50 | µm |
| Tensile Modulus | MD，50 µm MD : 50 µm | ISO 527-3 | 400 | Mpa |
| Tensile Modulus | TD，50 µm TD : 50 µm | ISO 527-3 | 400 | Mpa |
| Tensile Strength | MD，Yield，51 μm MD : Yield, 2.0 mil | ISO 527-3 | 30 | Mpa |
| Tensile Strength | TD，Yield，51 μm TD : Yield, 2.0 mil | ISO 527-3 | 30 | Mpa |
| Tensile Strain | MD，Break，50 μm MD : Break, 2.0 mil | ISO 527-3 | 540 | % |
| Tensile Strain | TD，Break，50 μm TD : Break, 2.0 mil | ISO 527-3 | 600 | % |
| Instrumented Puncture Test | | ISO 7765-2 | 320 | J/cm |
| Optical | Test Condition | Test Method | Test Result | Unit |
|---|
| Gloss | 20°，50 µm 20°，50.0 µm | ASTM D2457 | > 140 | |
| Haze | 50 µm 50.0 µm | ASTM D1003 | < 1.0 | % |
| Thermal | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Temperature | | ISO 11357-3 | 140 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.