Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 230°C/2.16kg | ISO1133 | 7.0 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Elongation?(Break) | | ISO 527 | 200 | |
| Heat Deflection Temperature | | ISO 75 | 80 | °C |
| Tensile Modulus | | ISO527-2 | 850 | Mpa |
| Tensile Strength | | ISO 527 | 23 | Mpa |
| hardness | R-Scale | ISO 2039-2 | 85 | |
| Tensile Stress | Yield | ISO527-2 | 23.0 | Mpa |
| Tensile Strain | Break | ISO527-2 | >200 | % |
| Izod notch impact strength | 23℃ | ISO 179 | 12 | kJ/m² |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 80.0 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179 | 12 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R-Sale | ISO2039-2 | 85 | |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 230℃ | ISO 1133 | 7 | g/10min |
| Density | | ISO 1183 | 0.910 | g/cm³ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.