Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 0.91 | |
Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 9.0 | g/10min |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt index | 230℃,2.16kg | ISO 1133 | 9.0 | g/10min |
Melt Mass-Flow Rate | 230°C/2.16kg | ISO1133 | 9.0 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Breaking tensile strain | | ISO 527-2 | 50 | % |
Tensile Stress | Yield | ISO527-2 | 29.0 | Mpa |
Tensile Strain | Break | ISO527-2 | 50 | % |
Tensile Stress(Yield) | | ISO 527-2 | 29 | Mpa |
Charpy Notched Impact Strength | -20℃ | ISO 179 | 4.0 | kJ/m² |
Charpy Notched Impact Strength | 23℃ | ISO 179 | 10 | kJ/m² |
Tensile Elongation?(Break) | | ASTM D638/ISO 527 | 50 | % |
Tensile Modulus | | ASTM D638/ISO 527 | 1450 | kg/cm²(MPa)[Lb/in²] |
Tensile Modulus | | ISO527-2 | 1450 | Mpa |
Tensile Modulus | | ISO 527-2 | 1450 | Mpa |
Tensile Strength | | ASTM D638/ISO 527 | 29 | kg/cm²(MPa)[Lb/in²] |
Rockwell Hardness | | ASTM D785 | 95 | |
Rockwell Hardness | | ISO 2039-2 | 95 | |
Izod notch impact strength | | ASTM D256/ISO 179 | 10 | kg·cm/cm(J/M)ft·lb/in |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO 75-2/B | 105 | °C |
Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 105 | ℃(℉) |
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 105 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -20°C | ISO179 | 4.0 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179 | 10 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | | ISO2039-2 | 95 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.