Technical Data Sheet
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Modulus | | ASTM D790 | 1270 | Mpa |
| hardness | R-Scale | ASTM D785 | 70 | |
| Tensile Strength | Yield | ASTM D638 | 28.4 | Mpa |
| Tensile Strength | Break | ASTM D638 | 19.6 | Mpa |
| Tensile Elongation | | ASTM D638 | 150 | % |
| Notched Izod Impact Strength | 0℃ | ASTM D256 | 39.2 | |
| Notched Izod Impact Strength | -20℃ | ASTM D256 | 29.4 | |
| Notched Izod Impact Strength | 23℃ | ASTM D256 | 78.5 | |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ASTM D1525 | 150 | °C |
| Brittleness Temperature | | ASTM D746 | -20 | °C |
| Melting temperature | | ASTM D2117 | 120-163 | °C |
| Deflection Temperature Under Load? | 0.45Mpa, Unannealed | ASTM D648 | 110 | °C |
| Deflection Temperature Under Load? | 1.8Mpa, Unannealed | ASTM D648 | 55 | °C |
| Other | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | | UL 94 | HB | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Gloss | | ASTM D2457 | 30 | |
| Haze | | ASTM D1003 | 80 | % |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Density / Specific Gravity | | ASTM D1505 | 0.91 | g/cm³ |
| Melt Mass-Flow Rate | 230°C/2.16 kg | ASTM D1238 | 27 | g/10min |
| Modeling Shrinkage | Across Flow: (2.00 mm) | ASTM D955 | 1.2 | % |
| Modeling Shrinkage | Flow: (2.00 mm) | ASTM D955 | 1.4 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.