Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 230°C/2.16kg | ASTMD1238 | 0.25 | g/10min |
| Ash Content | | ASTMD5630 | <300 | ppm |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Elongation | Break | ASTMD638 | >600 | % |
| Flexural Modulus | | ASTMD790 | 834 | Mpa |
| Tensile Strength | Yield | ASTMD638 | 22.6 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ASTMD1525 | 133 | °C |
| Peak Melting Temperature | | ASTMD3418 | 139 | °C |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ASTMD648 | 85.0 | °C |
| Oxidation Induction Time | 200°C | ASTMD3895 | >30 | min |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R-Scale | ASTMD785 | 72 | |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|
| MinimumRequiredStrength | | ISO9080 | 11.2 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.