Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 0.910 | |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 230°C/2.16kg | ISO1133 | 15 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Yield | ISO527-2 | 35.0 | Mpa |
Tensile Strain | Break | ISO527-2 | 100 | % |
Impact Strength | 23℃ | ISO 179 | 3.3 | kJ/m² |
Tensile Elongation?(Break) | | ASTM D638/ISO 527 | 100 | % |
Tensile Modulus | | ISO527-2 | 1600 | Mpa |
Tensile Strength | | ASTM D638/ISO 527 | 35.0 | kg/cm²(MPa)[Lb/in²] |
Tensile Strength | | ISO 527 | 35.0 | Mpa |
Tensile Elongation | Break | ISO 527 | 100 | % |
Rockwell Hardness | | ASTM D785 | 100 | |
Rockwell Hardness | | ISO 2039-2 | 100 | R scale |
Flexural Modulus | | ASTM D790/ISO 178 | 1600 | kg/cm²(MPa)[Lb/in²] |
Flexural Modulus | | ISO 527 | 1600 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 100 | °C |
Deflection Temperature Under Load? | 0.45MPa | ISO 75 | 100 | °C |
Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 120 | ℃(℉) |
Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 100 | ℃(℉) |
Melting Temperature | | | 15 | ℃(℉) |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO179 | 3.3 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Sale | ISO2039-2 | 100 | |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ISO 1183 | 0.910 | g/cm³ |
Melt index | 230℃ | ISO 1133 | 15 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.